Sustainability in the construction industry refers to all resource-efficient and environmentally responsible processes throughout the life cycle of a structure. Green buildings may incorporate reused, recycled, or recovered materials in their construction. Concrete is as an important building material. Due to the implementation of by-products and waste from various industries into its structure, concrete represents a significant sustainable material. Steel slag has great potential for its reuse in concrete production. Despite its volume changes over time, steel slag can be applied in concrete as a cement replacement (normally) or as a substitute for natural aggregates (rarely). This paper focused on an investigation of concrete with steel slag as a substitute of natural gravel aggregate. Testing physical and mechanical properties of nontraditional concrete with steel slag as a substitute for natural aggregates of 4/8 mm and 8/16 mm fractions confirmed the possibility of using slag as a partial replacement of natural aggregate. Several samples of concrete with steel slag achieved even better mechanical parameters (e.g., compressive strength, frost resistance) than samples with natural aggregate. Moreover, a life cycle assessment (LCA) was performed within the system boundaries cradle-to-gate. The LCA results showed that replacements of natural aggregates significantly affected the utilization rate of nonrenewable raw materials and reduced the overall negative impacts of concrete on the environment up to 7%. The sustainability indicators (SUI), which considered the LCA data together with the technical parameters of concrete, were set to evaluate sustainability of the analyzed concretes. Based on the SUI results, replacing only one fraction of natural gravel aggregate in concrete was a more sustainable solution than replacing both fractions at once. These results confirmed the benefits of using waste to produce sustainable materials in construction industry.

This article summarizes the results of a research study that was focused on the possibility of removing Cr (VI) from aqueous solution, using low-cost waste biomaterial in a batch mode. A set of seven biosorbents was used: Fomitopsis pinicola, a mixture of cones, peach stones, apricot stones, Juglans regia shells, orange peels, and Merino sheep wool. Three grain fractions (fr. 1/2, fr. 0.5/1.0, and fr. 0/0.5 mm) of biosorbents were studied. The aim was to find the most suitable biosorbent that can be tested with real samples. The influence of other factors on the course of biosorption was studied as well (chemical activation of the biosorbent, pH value, rotation speed during mixing, temperature, and the influence of biosorbent concentration). The use of chemical activation and adjustment of the pH to 1.1 to 2.0 make it possible to increase their sorption capacity and, for some biosorbents, to shorten the exposure times. Two kinetic models were used for the analysis of the experimental data, to explain the mechanism of adsorption and its possible speed control steps: pseudo-first and pseudo-second-order. The pseudo-second-order kinetic model seems to be the most suitable for the description of the experimental data. The thermodynamic parameters suggest that the biosorption was endothermic and spontaneous. In the biosorption equilibrium study, the adsorption data were described by using Langmuir and Freundlich adsorption isotherms. The Langmuir model was applicable to describe the adsorption data of all biosorbents. Both models are suitable for chemically treated sheep fleece and peach stones.

This article deals with the use of photovoltaic panels at the end of their life cycle in cement composites. Attention is focused on the properties of cement composite after 100% replacement of natural aggregate with recycled glass from photovoltaic panels. This goal of replacing natural filler sources with recycled glass is based on the updated policy of the Czech Republic concerning secondary raw materials for the period of 2019–2022, which aims to increase the self-sufficiency of the Czech Republic in raw materials by replacing primary sources with secondary raw materials. The policy also promotes the use of secondary raw materials as a tool to reduce the material and energy demands of industrial production and supports the innovations and development of a circular economy within business. The research has shown that it is possible to prepare cement composite based on recycled glass from solar panels, with compressive and flexural strength after 28 days exceeding 40 MPa and 4 MPa. Furthermore, a possible modification of the cement composite with different pigments has been confirmed, without disrupting the contact zone.

This article describes an experimental study aimed at investigating the potential use of recycled rubber granulate from waste tires of fractions 0/1 and 1/3 mm in cement composites as a 100% replacement for natural aggregates. The use of waste in the development and production of new building materials represents an important aspect for the sustainability and protection of the environment. This article is focused on the sound-absorbing and thermal-insulating properties of experimental cement composites based on recycled rubber from waste tires. The article describes the grain characteristics of recycled rubber, sound absorption capacity, thermal conductivity and strength characteristics. The results of this research show that the total replacement of natural aggregate with recycled rubber in cement composites is possible. Replacing natural aggregate with recycled rubber has significantly improved the thermal and acoustic properties of the prepared cement composites, however, at the same time; there was also the expected decrease in the strength characteristics due to the elasticity of rubber.

This article presents the results of a study dealing with the utilization of sludge water from a concrete plant as a partial replacement for mixing water in the production of cement composites. The replacement of mixing water with sludge water from a concrete plant was carried out in the amounts of 20% and 50%. The following tests were carried out in order to determine the effect of the replacement of mixing water with sludge water from a concrete plant on the physical and mechanical properties of the cement composites: cement mortar consistency, beginning and end of setting, strength characteristics (compressive strength and flexural strength), and thermal properties. The measured values of the strength characteristics of the test specimens after 28 days of age confirm the possibility of replacing mixing water with sludge water from a concrete plant without significantly reducing the compressive and flexural strength.

This paper aims to develop recycled fiber reinforced cement plaster mortar with a good workability of fresh mixture, and insulation, mechanical and adhesive properties of the final hardened product for indoor application. The effect of the incorporation of different portions of three types of cellulose fibers from waste paper recycling into cement mortar (cement/sand ratio of 1:3) on its properties of workability, as well as other physical and mechanical parameters, was studied. The waste paper fiber (WPF) samples were characterized by their different cellulose contents, degree of polymerization, and residues from paper-making. The cement to waste paper fiber mass ratios (C/WPF) ranged from 500:1 to 3:1, and significantly influenced the consistency, bulk density, thermal conductivity, water absorption behavior, and compressive and flexural strength of the fiber-cement mortars. The workability tests of the fiber-cement mortars containing less than 2% WPF achieved optimal properties corresponding to plastic mortars (140–200 mm). The development of dry bulk density and thermal conductivity values of 28-day hardened fiber-cement mortars was favorable with a declining C/WPF ratio, while increasing the fiber content in cement mortars led to a worsening of the water absorption behavior and a lower mechanical performance of the mortars. These key findings were related to a higher porosity and weaker adhesion of fibers and cement particles at the matrix-fiber interface. The adhesion ability of fiber-cement plastering mortar based on WPF samples with the highest cellulose content as a fine filler and two types of mixed hydraulic binder (cement with finely ground granulated blast furnace slag and natural limestone) on commonly used substrates, such as brick and aerated concrete blocks, was also investigated. The adhesive strength testing of these hardened fiber-cement plaster mortars on both substrates revealed lime-cement mortar to be more suitable for fine plaster. The different behavior of fiber-cement containing finely ground slag manifested in a greater depth of the plaster layer failure, crack formation, and in greater damage to the cohesion between the substrate and mortar for the observed time.