Starches from six different species (cassava, arrowroot, sweet potato, yam, canna and ginger) were isolated and some structural and physicochemical characteristics analysed and correlated. Phosphorous and amylose contents were determined using a colorimetric method and measuring iodine affinity, respectively. Molecular weight distributions of starches were analysed by Sepharose CL 2B. Granular shape and size distribution were performed using an image analyser system attached to a light microscope. Swelling power was determined at 60, 70, 80 and 90°C. Pasting and thermal properties were measured using a rapid viscoanalyser, and a differential scanning calorimeter, respectively. Phosphorous content varied from 0.007 to 0.031% for cassava and canna starches, respectively. Yam, canna and ginger starches displayed higher amylose contents (32.6, 31.7 and 26.5%, respectively) than cassava, arrowroot and sweet potato starches (19.8, 20.8 and 22.6%, respectively). These last three starches displayed amylose molecules of higher molecular weight than those shown for yam, canna and ginger starches. Canna starch showed higher proportions of longer branch chains of amylopectin than others starches. The size and shape of granules were quite variable among all starches and the average size of granules varied from 13.9 to 42.3μ for sweet potato and canna, respectively. Swelling power, pasting, and thermal properties were affected by structural characteristics of the starches.

Enzymatic hydrolysis of granular starch is an important tool to provide information about granule structure. Cassava, sweet potato, Peruvian carrot, and potato starches were hydrolyzed by bacterial α-amylase at 37 °C for 48 hours, and the physicochemical properties of the residues from hydrolysis were determined. Cassava starch was the most susceptible to enzyme displaying 20.9% of hydrolysis, whereas potato starch was the most resistant with 5.9%. The granule average size varied from 10.8 to 23.4 μm for Peruvian carrot and potato starches, respectively. With the use of SEM, a smooth granule surface was observed for all native starches. Cassava and sweet potato starches displayed an A-type X-ray diffraction pattern, while Peruvian carrot and potato starches showed a B-type pattern. After hydrolysis, cassava, sweet potato, and Peruvian carrot starches showed some well degraded granules, whereas potato starch presented a slight sign of degradation. The amylose content of the starches decreased with hydrolysis for cassava, sweet potato, and Peruvian carrot starches and was kept unchanged for the potato starch. As expected, intrinsic viscosity and pasting properties decreased for all hydrolyzed starches. There is no difference between thermal properties of native and hydrolyzed starches. These results suggested that hydrolysis occurred in amorphous and crystalline areas of the granules. The B type diffraction pattern in conjunction with the big granule size of the potato starch may have contributed to the greatest resistance of this starch to hydrolysis.