In this study, the morphological properties of g-C₃N₄ in g-C₃N₄-Pt photocatalysts were modified by a simple hydrothermal treatment for photocatalytic hydrogen evolution. In addition, the morphological modification effect of g-C₃N₄ on the hydrogen evolution performance was investigated. The long-time hydrothermal treatment clearly changed the morphology of g-C₃N₄ by building extended melem units with more oxygen functional groups at the defect edges of the extended melem units, which was evidenced by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS) measurements. The different morphological features of g-C₃N₄ resulted in lower photoluminescence (PL) emission intensity in PL spectra and a smaller semicircle radius in electrochemical impedance spectroscopy (EIS) data. This indicates the more efficient charge separation of the g-C₃N₄-Pt photocatalyst with a modified morphology. Consequently, morphologically modified g-C₃N₄-Pt showed a higher photocatalytic hydrogen evolution rate due to the better charge separation efficiency.

In this study, we synthesized Pt/g-C₃N₄ photocatalysts modified by a solvent etching process where ethanol (Pt/CN0), water (Pt/CN100), and a 50:50 mixture (Pt/CN50) were used as a solvent, and investigated the optimal properties of g-C₃N₄ to prepare the best Pt/g-C₃N₄ for photocatalytic hydrogen evolution. From diverse characterizations, water was proven to be a stronger solvent agent, resulting in not only the introduction of more O-functional groups onto the g-C₃N₄ surface, but also the degradation of a regular array of tri-s-triazine units in the g-C₃N₄ structure. While the addition of O-functional groups positively influenced the oxidation state of the Pt cocatalyst and the hydrogen production rate, the changes to g-C₃N₄ structure retarded charge transfer on its surface, inducing negative effects such as fast recombination and less oxidized Pt species. Pt/CN50 that was synthesized with the 50:50 solvent mixture exhibited the highest hydrogen production rate of 590.9 µmol g⁻¹h⁻¹, while the hydrogen production rates of Pt/CN0 (with pure ethanol solvent) and Pt/CN100 (with pure water solvent) were 462.7, and 367.3 µmol g⁻¹h⁻¹, respectively.

In this work, the growth of extended tri-s-triazine units (melem units) on g-C₃N₄ (CN) by hydrothermal treatment and its effect on the photodegradation efficiency of tetracycline hydrochloride (TC) is investigated. The CN-180-x and CN-200-6 samples were prepared using different hydrolysis times and temperatures, and they were characterized by multiple physicochemical techniques. In addition, their photodegradation performance was evaluated under visible light irradiation. Compared to the CN, CN-180-6 possesses remarkable photocatalytic degradation efficiency at 97.17% towards TC removal in an aqueous solution. The high visible-light-induced photo-reactivity of CN-180-6 directly correlates to charge transfer efficiency, numerous structural defects with a high specific surface area (75.0 m² g⁻¹), and sufficient O-functional groups over g-C₃N₄. However, hydrothermal treatment at a higher temperature or during a longer time additionally induces the growth of extended melem units on the surface of g-C₃N₄, resulting in the inhibition of the charge transfer. In addition, the superoxide radical is proven to be generated from photoexcited reaction and plays a key role in the TC degradation.