X-rays are widely used in probing inside information nondestructively, enabling broad applications in the medical radiography and electronic industries. X-ray imaging based on emerging lead halide perovskite scintillators has received extensive attention recently. However, the strong self-absorption, relatively low light yield and lead toxicity of these perovskites restrict their practical applications. Here, we report a series of nontoxic double-perovskite scintillators of Cs₂Ag_0.6Na_0.4In_1-yBi_yCl₆. By controlling the content of the heavy atom Bi³⁺, the X-ray absorption coefficient, radiative emission efficiency, light yield and light decay were manipulated to maximise the scintillator performance. A light yield of up to 39,000 ± 7000 photons/MeV for Cs₂Ag_0.6Na_0.4In_0.85Bi_0.15Cl₆ was obtained, which is much higher than that for the previously reported lead halide perovskite colloidal CsPbBr₃ (21,000 photons/MeV). The large Stokes shift between the radioluminescence (RL) and absorption spectra benefiting from self-trapped excitons (STEs) led to a negligible self-absorption effect. Given the high light output and fast light decay of this scintillator, static X-ray imaging was attained under an extremely low dose of ∼1 μGy_air, and dynamic X-ray imaging of finger bending without a ghosting effect was demonstrated under a low-dose rate of 47.2 μGy_air s⁻¹. After thermal treatment at 85 °C for 50 h followed by X-ray irradiation for 50 h in ambient air, the scintillator performance in terms of the RL intensity and X-ray image quality remained almost unchanged. Our results shed light on exploring highly competitive scintillators beyond the scope of lead halide perovskites, not only for avoiding toxicity but also for better performance.

All‐inorganic perovskite quantum dots (QDs) CsPbX₃ (X = Cl, Br, and I) have recently emerged as a new promising class of X‐ray scintillators. However, the instability of perovskite QDs and the strong optical scattering of the thick opaque QD scintillator film imped it to realize high‐quality and robust X‐ray image. Herein, the europium (Eu) doped CsPbBr₃ QDs are in situ grown inside transparent amorphous matrix to form glass‐ceramic (GC) scintillator with glass phase serving as both matrix and encapsulation for the perovskite QD scintillators. The small amount of Eu dopant optimizes the crystallization of CsPbBr₃ QDs and makes their distribution more uniform in the glass matrix, which can significantly reduce the light scattering and also enhance the photoluminescence emission of CsPbBr₃ QDs. As a result, a remarkably high spatial resolution of 15.0 lp mm⁻¹ is realized thanks to the reduced light scattering, which is so far a record resolution for perovskite scintillator based X‐ray imaging, and the scintillation stability is also significantly improved compared to the bare perovskite QD scintillators. Those results provide an effective platform particularly for the emerging perovskite nanocrystal scintillators to reduce light scattering and improve radiation hardness.