The silver particles were grown in situ on the surface of wood by the silver mirror method and modified with stearic acid to acquire a surface with superhydrophobic and antibacterial properties. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and X-ray energy spectroscopy (XPS) were used to analyze the reaction mechanism of the modification process. Scanning electron microscopy (SEM) and contact angle tests were used to characterize the wettability and surface morphology. A coating with a micro rough structure was successfully constructed by the modification of stearic acid, which imparted superhydrophobicity and antibacterial activity to poplar wood. The stability tests were performed to discuss the stability of its hydrophobic performance. The results showed that it has good mechanical properties, acid and alkali resistance, and UV stability. The durability tests demonstrated that the coating has the function of water resistance and fouling resistance and can maintain the stability of its hydrophobic properties under different temperatures of heat treatment.

In this paper, the waterborne UV lacquer product (WUV) was used as the main raw material, zinc oxide (ZnO) was used as the additive, and the stearic acid as the surface modifier. According to the method of spraying coating on the surface of poplar wood (Populus tomentosa), a simple and efficient preparation method was carried out to generate a super-hydrophobic surface and enhance the erosion resistance of the coating. By testing, the contact angle (CA) of water on the coating surface can reach 158.4°. The microstructure and chemical composition of the surface of coatings were studied by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), and X-ray diffraction (XRD). The results showed that under acidic conditions, the non-polar long chain alkyl group of stearic acid vapor molecule reacted with the hydroxyl group in acetic acid, the metal ions of the ZnO were displaced to the stearic acid and generated globular zinc stearate (C₃₆H₇₀O₄Zn). The hydrophobic groups –CH₃ were grafted to the surface of zinc stearate (ZnSt2) particles and the micro/nano level of multistage flower zinc stearate coarse structure was successfully constructed on the surface of poplar wood, which endowed it with superhydrophobic properties. It is shown that the coating has good waterproof and erosion resistance.

In this study, the microstructure and mechanical properties of poplar (Populus tomentosa) catkin fibers (PCFs) were investigated using field emission scanning electron microscope, atomic force microscopy (AFM), X-ray diffraction, and nanoindentation methods. Experimental results indicated that PCFs had a thin-wall cell structure with a large cell lumen and the hollow part of the cell wall took up 80 percent of the whole cell wall. The average diameters of the fiber and cell lumen, and the cell wall thickness were 5.2, 4.2, and 0.5 µm, respectively. The crystallinity of fibers was 32%. The AFM images showed that the orientation of microfibrils in cell walls was irregular and their average diameters were almost between 20.6–20.8 nm after being treated with 2 and 5 wt.% potassium hydroxide (KOH), respectively. According to the test of nanoindentation, the average longitudinal-reduced elastic modulus of the PCF S₂ layer was 5.28 GPa and the hardness was 0.25 GPa.

Masson pine (Pinus massoniana Lamb.) samples were heat-treated at different treatment temperatures (150, 170, and 190 °C), and the nano-mechanical properties of the wood cell wall, which was coated with a waterborne polyacrylic (WPA) lacquer product, were compared. The elastic modulus (E_r) and hardness (H) of wood cell wall and the coating were measured and characterized by nanoindentation, and the influencing factors of mechanical properties during thermal modification were investigated by chemical composition analysis, contact angle analysis, and colorimetric analysis. The results showed that with the increase in the heat treatment temperature, the contact angle of the water on the wood’s surface and the colorimetric difference increased, while the content of the cellulose and hemicelluloses decreased. After thermal modification of 190 °C, the E_r and H of the wood cell wall increased by 13.9% and 17.6%, respectively, and the E_r and H of the WPA coating applied to the wood decreased by 12.1% and 22.2%. The E_r and H of the interface between the coating and wood were lower than those near the coating’s surface. The E_r and H of the cell wall at the interface between the coating and wood were lower than those far away from the coating. This study was of great significance for understanding the binding mechanism between coating and wood cell walls and improving the finishing technology of the wood materials after thermal modification.