This study developed a nano-magnetite-modified biochar material (m-biochar) using a simple and rapid in situ synthesis method via microwave treatment, and systematically investigated the removal capability and mechanism of chromium (VI) by this m-biochar from contaminated groundwater. The m-biochar was fabricated from reed residues and magnetically modified by nano-Fe₃O₄. The results from scanning electron microscopy (SEM) and X-ray diffraction (XRD) characterisations confirmed the successful doping of nano-Fe₃O₄ on the biochar with an improved porous structure. The synthesised m-biochar exhibited significantly higher maximum adsorption capacity of 9.92 mg/g compared with that (8.03 mg/g) of the pristine biochar. The adsorption kinetics followed the pseudo-second-order model and the intraparticle diffusion model, which indicated that the overall adsorption rate of Cr(VI) was governed by the processes of chemical adsorption, liquid film diffusion and intramolecular diffusion. The increasing of the pH from 3 to 11 significantly affected the Cr(VI) adsorption, where the capabilities decreased from 9.92 mg/g to 0.435 mg/g and 8.03 mg/g to 0.095 mg/g for the m-biochar and pristine biochar, respectively. Moreover, the adsorption mechanisms of Cr(VI) by m-biochar were evaluated and confirmed to include the pathways of electrostatic adsorption, reduction and complexation. This study highlighted an effective synthesis method to prepare a superior Cr(VI) adsorbent, which could contribute to the effective remediation of heavy metal contaminations in the groundwater.

Harmful algal blooms are a global problem in water environments, and their explosive growth endangers the health of aquatic ecosystems. Magnetic nanomaterials for the harvesting of microalgae have received a lot of attention because of their high efficiency, low cost, and ease of operation. In this study, magnetic mesoporous silica nanomaterials were prepared using Fe₃O₄ as a carrier and harvesting on Chlorella sp. HQ. It was found that silica coated with magnetic Fe₃O₄ microspheres has good dispersion. The harvesting of Chlorella sp. HQ via magnetic mesoporous silica could be maintained over a wide pH range (4 to 12). After the removal of organic components from the surface of the material, the magnetic mesoporous silica obtained a better porous structure. The ethanol reflux method was more beneficial than the calcination method in maintaining the stable structure of the material, thus improving the harvesting efficiency of the material for the microalgae Chlorella sp. HQ by a maximum of 17.8% (65.9% to 83.7%). When the molar ratio of active agent cetyltrimethylammonium bromide (CTAB) and stabilizer polyvinylpyrrolidone (PVP) was 1: 0.092 at pH 4 and algal concentration of 0.5 g/L, the materials showed the maximum harvesting efficiency of Chlorella sp. HQ was 84.2%.