Preparation of magnetic nanoparticles coated with chitosan (CS-coated Fe₃O₄ NPs) in one step by the solvothermal method in the presence of different amounts of added chitosan is reported here. The magnetic property of the obtained magnetic composite nanoparticles was confirmed by X-ray diffraction (XRD) and magnetic measurements (VSM). Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) allowed the identification of spherical nanoparticles with about 150 nm in average diameter. Characterization of the products by Fourier transform infrared spectroscopy (FTIR) demonstrated that CS-coated Fe₃O₄ NPs were obtained. Chitosan content in the obtained nanocomposites was estimated by thermogravimetric analysis (TGA). The adsorption properties of the CS-coated Fe₃O₄ NPs for bovine serum albumin (BSA) were investigated under different concentrations of BSA. Compared with naked Fe₃O₄ nanoparticles, the CS-coated Fe₃O₄ NPs showed a higher BSA adsorption capacity (96.5 mg/g) and a fast adsorption rate (45 min) in aqueous solutions. This work demonstrates that the prepared magnetic nanoparticles have promising applications in enzyme and protein immobilization.

A facile one-step synthesis of CdTe quantum dots (QDs) in aqueous solution by atmospheric microwave reactor has been developed using 3-mercaptopropionic acid reduction of TeO2 directly. The obtained CdTe QDs were characterized by ultraviolet–visible spectroscopy, fluorescent spectroscopy, X-ray powder diffraction, multifunctional imaging electron spectrometer (XPS), and high-resolution transmission electron microscopy. Green- to red-emitting CdTe QDs with a maximum photoluminescence quantum yield of 56.68% were obtained.

Hydrogel adhesives are attractive for applications in intelligent soft materials and tissue engineering, but conventional hydrogels usually have poor adhesion. In this study, we designed a strategy to synthesize a novel adhesive with a thin hydrogel adhesive layer integrated on a tough substrate hydrogel. The adhesive layer with positive charges of ammonium groups on the polymer backbones strongly bonds to a wide range of nonporous materials’ surfaces. The substrate layer with a dual hydrogen bond system consists of (i) weak hydrogen bonds between N,N-dimethyl acrylamide (DMAA) and acrylic acid (AAc) units and (ii) strong multiple hydrogen bonds between 2-ureido-4[1H]-pyrimidinone (UPy) units. The dual hydrogen-bond network endowed the hydrogel adhesives with unique mechanical properties, e.g., toughness, highly stretchability, and insensitivity to notches. The hydrogel adhesion to four types of materials like glass, 316L stainless steel, aluminum, Al₂O₃ ceramic, and two biological tissues including pig skin and pig kidney was investigated. The hydrogel bonds strongly to dry solid surfaces and wet tissue, which is promising for biomedical applications.

Sustainable conversion of CO₂ to fuels using solar energy is highly attractive for fuel production. This work focuses on the synthesis of porous graphitic carbon nitride nanobelt catalyst (PN-g-C₃N₄) and its capability of photocatalytic CO₂ reduction. The surface area increased from 6.5 m²·g⁻¹ (graphitic carbon nitride, g-C₃N₄) to 32.94 m²·g⁻¹ (PN-g-C₃N₄). C≡N groups and vacant N_2C were introduced on the surface. PN-g-C₃N₄ possessed higher absorbability of visible light and excellent photocatalytic activity, which was 5.7 and 6.3 times of g-C₃N₄ under visible light and simulated sunlight illumination, respectively. The enhanced photocatalytic activity may be owing to the porous nanobelt structure, enhanced absorbability of visible light, and surface vacant N-sites. It is expected that PN-g-C₃N₄ would be a promising candidate for CO₂ photocatalytic conversion.