Blasting excavation of rock masses under high in-situ stress often encounters difficulties in rock fragmentation and a high boulder rate. To gain a deeper understanding of this issue, the stress distribution of rock masses under dynamic and static loads was first studied through theoretical analysis. Then, the ANSYS/LS-DYNA software was employed to simulate the blasting crack propagation in rock masses under various in-situ stress conditions. The fractal dimension was introduced to quantitatively analyze the influence of in-situ stress on the distribution of blasting cracks. The results indicate that in-situ stress primarily affects crack propagation in the later stages of the explosion, while crack initiation and propagation in the early stages are mainly driven by the explosion load. In-situ stress significantly influences the damage area and fractal dimension of cut blasting. Under hydrostatic in-situ stress, as the in-situ stress increases, the damage area and fractal dimension of blasting cracks gradually decrease. Under non-hydrostatic in-situ stress, when the principal stress difference is small, in-situ stress promotes the damage area and fractal dimension of the surrounding rock, enhancing rock fragmentation. However, when the principal stress difference is large, in-situ stress inhibits the damage area and fractal dimension of the surrounding rock, hindering effective rock breaking.

To study the dynamic tensile mechanical properties of steel polypropylene hybrid fiber reinforced concrete (SP-HFRC) after high temperature, split Hopkinson pressure bar (SHPB) dynamic splitting tests were carried out, and the optimal fiber content combination was obtained. With the plain concrete (PC) as the control, the effects of fiber addition on energy dissipation and failure forms of concrete specimens after high temperatures were analyzed. LS-DYNA software was used to simulate the dynamic splitting test. The results show that the splitting strength of specimens increases first and then deteriorates with the increase of temperature. After high temperatures, HFRC has a positive and negative fiber hybrid effect. Among the studied fiber mixture combinations, S1PP0.2 (1 vol% steel fiber + 0.2 vol% polypropylene fiber) concrete has the best splitting resistance. Compared with PC, the splitting strength increases by 106.8% at 25 °C and 128.2% at 800 °C. From the perspective of energy, we can conclude that adding hybrid fiber can significantly improve the dynamic splitting and tensile toughness of concrete after high temperatures, and defining damage variables can better characterize the damage degree of concrete. PC cracks seriously after high temperatures, while S1PP0.2 concrete cracks but does not disperse at 800 °C, showing ductile failure characteristics. By modifying some parameters of the HJC model, the state of high-temperature concrete mechanical properties can be better characterized after deterioration. The simulated failure process shows an excellent agreement with the experimental results.

The one-time completion blasting technology for blind shafts is widely used in underground mining, for safety reasons. Efficient blind shaft excavation relies on reasonable cutting blasting technology. To optimize blasting parameters, the impact of explosion stress waves and gases on rock fragmentation is quantitatively analyzed using explosion stress wave theory. A calculation model for the radius R₁ of the crushed zone and the radius R₂ of the fractured zone in rock under the combined action of borehole cutting stress waves and blasting gases is derived and established. Combined with practical engineering examples and the determination method of compensation coefficient C_f, three types of linear cutting patterns, namely six-hole bucket cutting, seven-hole bucket cutting, and nine-hole bucket cutting, are designed. The post-blasting cavity volume and crack length of these three different cutting methods are calculated and analyzed using numerical simulation. Quantitative description of the distribution pattern of blasting-induced cracks in the simulation results of three cutting methods using the box-counting fractal dimension method are presented. Based on this analysis, the nine-hole bucket cutting is selected as the optimal scheme and validated through field application of cutting blasting. The results indicate that the nine-hole bucket cutting blasting scheme for one-time completion of blind shafts, with a designed hole depth of 8 m and a blasthole utilization rate of 93.7%, is an efficient and reasonable technical solution.