Biodegradable composite membranes containing propolis were produced from PCL/PLLA blends using a simple and low-cost solvent casting method, and subsequently their physicochemical, mechanical, and antibacterial properties were characterized. SEM analysis revealed that the addition of propolis has created honeycomb-like structures on the film surfaces. The flexibility of the films increased in the presence of propolis, which may provide ease of use during application. Propolis disrupted the organized structure of both polymers at the molecular level and caused decreases in the melting points. The films with propolis showed faster degradation in physiological conditions due to this molecular disruption. Moreover, the PLLA/PCL/propolis composite films exhibited remarkable antibacterial activities againstS. aureus. Collectively, the data suggest that the produced films might be used as an alternative to exiting barrier membranes in guided tissue regeneration.

The accurate mimicking of the fibrillary structure of the extracellular matrix represents one of the critical aspects of tissue engineering, playing a significant role in cell behavior and functions during the regenerative process. This work proposed the design of PVA-based multi-component membranes as a valuable and highly versatile strategy to support in vitro regeneration of different tissues. PVA can be successfully processed through electrospinning processes, allowing for the integration of other organic/inorganic materials suitable to confer additive bio-functional properties to the fibers to improve their biological response. It was demonstrated that adding polyethylene oxide (PEO) improves fiber processability; moreover, SEM analyses confirmed that blending PVA with PEO or gelatin enables the reduction of fiber size from 1.527 ± 0.66 μm to 0.880 ± 0.30 μm and 0.938 ± 0.245 μm, respectively, also minimizing defect formation. Furthermore, in vitro tests confirmed that gelatin integration allows the formation of bioactive nanofibers with improved biological response in terms of L929 adhesion and proliferation. Lastly, the processability of PVA fibers with conductive phases such as polyvinylpyrrolidone (PVP) or poly(3,4-ethylene dioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) has also been verified. From this perspective, they could be promisingly used to design electroactive composite fibers able to support the regeneration process of electrically stimulated tissues such as nerves or muscles.

Synthetic polymers remain to be a major choice for scaffold fabrication due to their structural stability and mechanical strength. However, the lack of functional moieties limits their application for cell-based therapies which necessitate modification and functionalization. Blending synthetic polymers with natural components is a simple and effective way to achieve the desired biological properties for a scaffold. Herein, nanofibrous mats made of polycaprolactone (PCL) and egg white protein (EWP) blend were developed and further evaluated for use as a scaffold for tissue engineering applications. Homogeneous distribution of EWP was achieved throughout the nanofibrous mats, as shown by immunohistochemistry. ATR-FTIR analysis and contact angle measurements have further confirmed the presence of EWP on the surface of the samples. The swelling test showed that PCL/EWP nanofibers have higher water uptake than PCL nanofibrous mats. Also, EWP addition on the nanofibrous mats resulted in an increase in the tensile strength and Young’s modulus of the mats, indicating that the presence of protein can greatly enhance the mechanical properties of the mats. A significantly higher, more uniform, and dispersed cell spreading was observed on days 7 and 14 than that on neat PCL mats, demonstrating the importance of providing the required cues for cell homing by the availability of EWP. Hence, EWP is shown to be a simple and low-cost source for the functionalization of PCL nanofibrous mats. EWP is, therefore, a facile candidate to enhance cellular interactions of synthetic polymers for a wide range of tissue engineering applications.

MXene‐based materials have gained attention in the biomedical field due to their promising biocompatibility, improved mechanical strength, and conductivity. In this study, the focus is on optimizing MXene‐incorporated electrospun fibers and subsequent characterizations to assess their potential for biomedical applications. Polyvinyl alcohol (PVA) is used as the appropriate matrix material and process parameters are finetuned to ensure effective incorporation of MXene. XRD and spectroscopic analysis confirm the successful synthesis and integration of MXenes into the nanofibers. Morphological analysis shows that MXene led to the formation of sub‐micrometer fibers with smooth surfaces and reduced the fiber diameter (587 ± 191 nm) compared to pure PVA (696 ±160 nm). Investigations on the electrical characteristics demonstrate a fourfold increase in conductivity of nanofibers (σ = 1.90 ± 0.45 × 10⁻⁸ S cm⁻¹) after MXene addition (compared to σ = 0.46 ± 0.05 × 10⁻⁸ S cm⁻¹ of PVA‐only fibers). Furthermore, the MXene‐PVA system demonstrates a nearly twofold increase in mechanical stiffness, with E = 136.87 ± 19.63 MPa than 71.42 ± 16.56 MPa for PVA. Moreover, the initial in vitro experiments indicate improved L929 cell viability. These findings position MXene‐PVA composites as a highly versatile platform for advanced biomedical devices, such as electroactive tissue scaffolds and wearable sensors.

The brain consists of an interconnected network of neurons tightly packed in the extracellular matrix (ECM) to form complex and heterogeneous composite tissue. According to recent biomimicry approaches that consider biological features as active components of biomaterials, designing a highly reproducible microenvironment for brain cells can represent a key tool for tissue repair and regeneration. Indeed, this is crucial to support cell growth, mitigate inflammation phenomena and provide adequate structural properties needed to support the damaged tissue, corroborating the activity of the vascular network and ultimately the functionality of neurons. In this context, electro-fluid dynamic techniques (EFDTs), i.e., electrospinning, electrospraying and related techniques, offer the opportunity to engineer a wide variety of composite substrates by integrating fibers, particles, and hydrogels at different scales—from several hundred microns down to tens of nanometers—for the generation of countless patterns of physical and biochemical cues suitable for influencing the in vitro response of coexistent brain cell populations mediated by the surrounding microenvironment. In this review, an overview of the different technological approaches—based on EFDTs—for engineering fibrous and/or particle-loaded composite substrates will be proposed. The second section of this review will primarily focus on describing current and future approaches to the use of composites for brain applications, ranging from therapeutic to diagnostic/theranostic use and from repair to regeneration, with the ultimate goal of providing insightful information to guide future research efforts toward the development of more efficient and reliable solutions.

In the last two decades, several processes have been explored for the development of micro and/or nanostructured substrates by sagely physically and/or chemically manipulating polymer materials. These processes have to be designed to overcome some of the limitations of the traditional ones in terms of feasibility, reproducibility, and sustainability. Herein, the primary aim of this work is to focus on the enormous potential of using a high voltage electric field to manipulate polymers from synthetic and/or natural sources for the fabrication of different devices based on elementary units, i.e., fibers or particles, with different characteristic sizes—from micro to nanoscale. Firstly, basic principles and working mechanisms will be introduced in order to correlate the effect of selected process parameters (i.e., an applied voltage) on the dimensional features of the structures. Secondly, a comprehensive overview of the recent trends and potential uses of these processes will be proposed for different biomedical and bio-sustainable application areas.