Corrosion at modular junctions of total hip replacement (THR) remains a major concern today. Multiple types of damage modes have been identified at modular junctions, correlated with different corrosion characteristics that may eventually lead to implant failure. Recently, within the head‐taper region of the CoCrMo retrieval implants, cell‐like features and trails of etching patterns were observed that could potentially be linked to the involvement of cells of the periprosthetic region. However, there is no experimental evidence to corroborate this phenomenon. Therefore, we aimed to study the potential role of periprosthetic cell types on corrosion of CoCrMo alloy under different culture conditions, including the presence of CoCrMo wear debris. Cells were incubated with and without CoCrMo wear debris (obtained from a hip simulator) with an average particle size of 119 ± 138 nm. Electrochemical impedance spectroscopy (EIS) was used to evaluate the corrosion tendency, corrosion rate, and corrosion kinetics using the media after 24 h of cell culture as the electrolyte. Results of the study showed that there was lower corrosion resistance (p < 0.02) and higher capacitance (p < 0.05) within cell media from macrophages challenged with particles when compared with the other media conditions studied. The potentiodynamic results were also in agreement with the EIS values, showing significantly higher corrosion tendency (low E_corr) (p < 0.0001) and high I_corr (p < 0.05) in media from challenged macrophages compared with media with H₂O₂ solution. Overall, the study provides in vitro experimental evidence for the possible role of macrophages in altering the chemical environment within the crevice and thereby accelerating corrosion of CoCrMo alloy. © 2019 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 38:393‐404, 2020

The frequency of surgeries involving the use of metal implants in orthopedic medicine to replace degenerative or fractured joints is increasing, and it is therefore important to optimize the lifespan and quality of these implants. Advances in additive manufacturing (AM), or 3D printing, are creating new opportunities to personalize implants in ways that reduce mechanical stress at the joint implant interface and improve bone ingrowth and implant stability; however, it is not well understood if and to what degree the AM process alters the corrosion behavior of the materials it produces. In this study, six Ti6Al4V prints manufactured via a selective laser melting (SLM) method were examined regarding their corrosion behavior in both saline and bovine calf serum (BCS) solutions. E_corr and I_corr values were comparable between the CM-Ti6Al4V control and SLM-EDM surfaces; however, SLM surfaces were found to have more narrow passivation behavior evidenced by significant decreases in E_pass values relative to CM-Ti6Al4V. We believe this is a consequence of microstructural differences between CM-Ti6Al4V and SLM-Ti6Al4V. Specifically, the SLM-Ti6Al4V demonstrated a dominant α′ martensitic microstructure and decreased vanadium-rich β-phase. BCS solution had a detrimental effect on potential parameters, E_corr and OCP, decreasing these values relative to their saline counterparts. Increased surface roughness of the SLM-printed surface seemed to amplify the effects of the BCS solution. Furthermore, modest decreases in E_pass and I_pass were observed in BCS solution, suggesting that the presence of protein may also interfere with passivation behavior. These findings have implications for how SLM-Ti6Al4V implants will perform in vivo and could possibly influence implant longevity and performance.

Diabetic retinopathy (DR), Retinopathy of Pre-maturity (ROP), and Age-related Macular Degeneration (AMD) are multifactorial manifestations associated with abnormal growth of blood vessels in the retina. These three diseases account for 5% of the total blindness and vision impairment in the US alone. The current treatment options involve heavily invasive techniques such as frequent intravitreal administration of anti-VEGF (vascular endothelial growth factor) antibodies, which pose serious risks of endophthalmitis, retinal detachment and a multitude of adverse effects stemming from the diverse physiological processes that involve VEGF. To overcome these limitations, this current study utilizes a micellar delivery vehicle (MC) decorated with an anti-angiogenic peptide (aANGP) that inhibits αvβ3 mediated neovascularization using primary endothelial cells (HUVEC). Stable incorporation of the peptide into the micelles (aANGP-MCs) for high valency surface display was achieved with a lipidated peptide construct. After 24 h of treatment, aANGP-MCs showed significantly higher inhibition of proliferation and migration compared to free from aANGP peptide. A tube formation assay clearly demonstrated a dose-dependent angiogenic inhibitory effect of aANGP-MCs with a maximum inhibition at 4 μg/mL, a 1000-fold lower concentration than that required for free from aANGP to display a biological effect. These results demonstrate valency-dependent enhancement in the therapeutic efficacy of a bioactive peptide following conjugation to nanoparticle surfaces and present a possible treatment alternative to anti-VEGF antibody therapy with decreased side effects and more versatile options for controlled delivery.