A graphitic layer is found to be the cause of low friction in metal-on-metal hip implants.

Recently, “tribocorrosion,” a research area combining the science of tribology and corrosion, has drawn attention from scientists and engineers belonging to a wide spectrum of research domains. This is due to its practical impact on daily life and also the accompanying economical burdens. It encompasses numerous applications including the offshore, space, and biomedical industry, for instance, in the case of artificial joints (Total Hip Replacement, THR) in orthopedic surgery, where implant metals are constantly exposed to tribological events (joint articulations) in the presence of corrosive solutions, that is, body fluids. Keeping the importance of this upcoming area of research in biomedical applications in mind, it was thought to consolidate the work in this area with some fundamental aspects so that a comprehensive picture of the current state of knowledge can be depicted. Complexity of tribocorrosion processes has been highlighted, as it is influenced by several parameters (mechanical and corrosion) and also due to the lack of an integrated/efficient test system. Finally a review of the recent work in the area of biotribocorrosion is provided, by focusing on orthopedic surgery and dentistry.

Wear of the modular taper between head and shaft has been related to clinical failure resulting from adverse reactions to metallic debris. The problem has become pronounced in large metal‐on‐metal bearings, but the mechanism has not yet been fully understood. We analyzed retrieved components from five patients revised with various diagnoses. Two distinct wear patterns were observed for the head tapers. Three samples demonstrated “asymmetric” wear towards the inner end of the head taper. The other two showed “axisymmetric” radial wear (up to 65 µm) presenting the largest wear volumes (up to 20 mm³). Stem tapers demonstrated relatively little wear, and the fine thread on the stem taper surface was observed to be imprinted on the taper inside of the head. Our findings demonstrate that the cobalt‐chrome head wears preferentially to the titanium stem taper. “asymmetric” wear suggests toggling due to the offset of the joint force vector from the taper. In contrast, samples with “axisymmetric” radial wear and a threaded imprint suggested that corrosion led to head subsidence onto the stem taper with gradual rotation. © 2013 Orthopaedic Research Society Published by Wiley Periodicals, Inc. J Orthop Res 31:1116–1122, 2013