This paper deals with the investigation of complex corrosion properties of 3D printed AISI 316L steel and the influence of additional heat treatment on the resulting corrosion and mechanical parameters. There was an isotonic solution used for the simulation of the human body and a diluted sulfuric acid solution for the study of intergranular corrosion damage of the tested samples. There were significant microstructural changes found for each type of heat treatment at 650 and 1050 °C, which resulted in different corrosion properties of the tested samples. There were changes of corrosion potential, corrosion rate and polarization resistance found by the potentiodynamic polarization method. With regard to these results, the most appropriate heat treatment can be applied to applications with intended use in medicine.

Anodization coloring of titanium tools or implants is one of the common methods for the differentiation of each application by its size or type. Commercial purity titanium grade 4 plates (50 × 20 × 0.1 mm) were tested to obtain their electrochemical and other technological properties. The coloring process was done using the potential of 15, 30, 45, 60, and 75 Volts for 5 s in 1 wt. % citric acid in demineralized water solution. Organic acids solutions generally produce better surface quality compared to inorganic acids. The contact angle of colored surfaces was measured by the sessile drop method. Electrochemical impedance spectroscopy and potentiodynamic polarization were used for the determination of selected electrochemical and corrosion parameters of the tested surfaces. It was found that the anodization process decreases corrosion potential significantly. It was also confirmed that a higher potential used for anodization results in higher polarization resistance but also a decrease in corrosion potential. The anodization process at 75 V produces surfaces with the lowest corrosion rate under 1 nm/year and the noblest corrosion potential. It was confirmed that the anodization process in citric acid does not affect titanium cytotoxicity.

In this paper corrosion properties and microstructure features of amorphous self-organised TiO2 nanotubes electrochemically deposited on titanium are discussed. There was titanium of second grade used as a substrate for these experiments. There was a specific solution of ammonium fluoride, ethylenglycol and deionized water used to create an oxide layer with advantageous properties. Relation between changes of roughness indexes before and after anodization was found out. The wettability (contact angle) of artificial plasma on surface was measured using sessile drop method. It was found out that titanium dioxide nanotubes formed on the surface significantly decreases contact angle and time of anodization reduces it even more. Corrosion potentials, corrosion rate or polarization resistance were determined by linear polarization methods performed by ASTM standards. Corrosion potential of anodized samples is substantially more positive (≈ -50mV) compared with non-treated sample (≈ - 280mV). On the other hand polarization resistance was significantly higher for non-treated sample. Also potentials of passive layer breakdowns were found. Structure of nanotubes and influence of anodization on surface profile was studied by SEM.

This study delves into selective laser melting (SLM). By using M300 steel in virgin and recycled powder form (after 20 cycles), with the aim of reducing the cost of printing for the practical application of M300 maraging steel, a comprehensive comparison between the two types of powder was evaluated. The powder’s morphology was analyzed using scanning electron microscopy (SEM) and backscattered electrons (BSE). The particles were seen to have a spherical shape, with a notable number of satellites attached to their surfaces. The particle size distribution (PSD) was examined and ranged from 10 to 90 µm for both powders. In addition, the porosity exhibited an average value of 0.07% for the virgin powder and 0.10% for the recycled powder. The microstructure was examined. Additionally, the surface wettability was tested, and it was seen to display wetting behavior for both types of powder, while blackened surfaces showed a higher wetting angle than untreated surfaces (hydrophobic). The 2D roughness measurements showed that the recycled powder had no significant difference from the virgin powder (Ra = 5.33 µm, Rz = 24.17 µm) before blackening and (Ra = 5.48 µm, Rz = 24.07 µm) after blackening. Corrosion tests proved that the recycled powder did not affect the corrosion properties of the material, while blackening caused partial surface corrosion in both types of samples, regardless of the used powder.