We show that the recombination energy of the direct band gap photoluminescence (PL) of germanium can be controlled by an external mechanical stress. The stress is provided by an apparatus commonly used for bulge or blister test. An energy redshift up to 60 meV is demonstrated for the room temperature PL of a thin germanium membrane (125 nm wavelength shift from 1535 to 1660 nm). This PL shift is correlated with the in-plane tensile strain generated in the film. A biaxial tensile strain larger than 0.6% is achieved by this method. This mechanical strain allows to approach the direct band gap condition for germanium which is of tremendous importance to achieve lasing with this material.

A novel structure of electrodynamics microelectromechanical systems (MEMS) microspeaker designed for mobile electronics is proposed in this paper. The originality of the device lies on the use of a rigid silicon membrane suspended by highly flexible silicon springs, contrary to most MEMS and non-MEMS microspeakers, which use polymer diaphragms. Important rigidity of the membrane and high linearity of the magnetic actuation conferred outstanding sound quality. The design of the silicon springs enabled large out-of-plane displacement of the membrane, which improved the bass rendering and the acoustic intensity over the whole bandwidth. The low density of silicon material helped to reduce the mobile mass and thus improved the microspeaker efficiency. A prototype with a membrane diameter of 15 mm and a thickness of 20 μm is microfabricated and characterized. The silicon springs enabled out-of-plane displacement of more than 300 μm. Acoustic intensity of 80-dB SPL is measured at 10 cm with 500-mW input power. This sound pressure level is obtained at frequencies from 330 Hz up to 70 kHz. Thanks to the membrane backside microstructure, most of the membrane proper modes are shifted out of the audible bandwidth. The measured electroacoustic efficiency is almost three times better than that of conventional microspeakers.

This paper reports on the study of microporous polydimethylsiloxane (PDMS) foams as a highly deformable dielectric material used in the composition of flexible capacitive pressure sensors dedicated to wearable use. A fabrication process allowing the porosity of the foams to be adjusted was proposed and the fabricated foams were characterized. Then, elementary capacitive pressure sensors (15 × 15 mm² square shaped electrodes) were elaborated with fabricated foams (5 mm or 10 mm thick) and were electromechanically characterized. Since the sensor responses under load are strongly non-linear, a behavioral non-linear model (first order exponential) was proposed, adjusted to the experimental data, and used to objectively estimate the sensor performances in terms of sensitivity and measurement range. The main conclusions of this study are that the porosity of the PDMS foams can be adjusted through the sugar:PDMS volume ratio and the size of sugar crystals used to fabricate the foams. Additionally, the porosity of the foams significantly modified the sensor performances. Indeed, compared to bulk PDMS sensors of the same size, the sensitivity of porous PDMS sensors could be multiplied by a factor up to 100 (the sensitivity is 0.14 %.kPa⁻¹ for a bulk PDMS sensor and up to 13.7 %.kPa⁻¹ for a porous PDMS sensor of the same dimensions), while the measurement range was reduced from a factor of 2 to 3 (from 594 kPa for a bulk PDMS sensor down to between 255 and 177 kPa for a PDMS foam sensor of the same dimensions, according to the porosity). This study opens the way to the design and fabrication of wearable flexible pressure sensors with adjustable performances through the control of the porosity of the fabricated PDMS foams.