The hygroscopic properties of thermally modified wood have been studied in terms of adsorption and desorption processes. Poplar (Populus spp.) and European beech (Fagus sylvatica L.) were in focus. The obtained isotherms were parameterized with the models of Hailwood-Horrobin, Guggenheim-Anderson-deBoer, generalized D’Arcy and Watt, and Yanniotis and Blahovec. The changes in equilibrium moisture content (EMC) were quantified, and the accessibility of water vapor to the sorption sites was determined. The monolayer and multilayer sorption was studied and the sorption isotherms were classified. All sorption isotherms were type II, and the type was not changed after the modification. The monolayer sorption was found to be responsible for the reduction in EMC after thermal modification. The observed increase in the hysteresis coefficient was explained by the reorganization of the wood ultrastructure.

Effects of Cyclic Changes in Relative Humidity on the Sorption Hysteresis of Thermally Modified Spruce Wood

Over the last decade, there has been increased interest in applying biomass as a raw material for producing biofuels used for thermochemical conversions. Extensive use of biomass could lead to controversial competition for arable land, water, and food; therefore, only waste materials and agricultural by-products and residues should be used to produce biofuels. One suitable by-product of agricultural production is crop residue from the harvest of maize for grain (corn stover). The harvest residues of corn stover consist of four fractions, i.e., husks, leaves, cobs, and stalks, which are structurally and morphologically distinct. The aim of the study was to determine the effect of selected maize cultivars with distinct FAO (Food and Agriculture Organization of the United Nations) earliness classifications on the chemical and energetic properties of their corn cob cores. We determined the chemical properties based on elemental analysis, and the energy properties based on the heat of combustion and calorific values. The content of ash and volatile compounds in the corn cobs were also determined. The results indicated that the heat of combustion of fresh and seasoned corn cob cores ranged from 7.62–10.79 MJ/kg and 16.19–16.53 MJ/kg, respectively. The heat of combustion and calorific value of corn cob cores in the fresh state differed significantly and were strongly correlated with maize cultivars with distinct FAO earliness.

European ash (Fraxinus excelsior L.) is one of the species commonly used for wood thermal modification that improves its performance. The presented research aimed to investigate a moisture-dependent strength anisotropy of thermally-modified European ash in compression. Wood samples were modified at 180 °C and 200 °C. Their mechanical parameters were determined in the principal anatomical directions under dry (moisture content of 3%) and wet (moisture content above fibre saturation point) conditions. Effect of heat treatment temperature and moisture content on the ash wood mechanical parameters concerning each anatomical direction were determined. The results show that thermal treatment kept the intrinsic anisotropy of wood mechanical properties. It decreased wood hygroscopicity, which resulted in improved strength and elasticity measured for wet wood when compared to untreated and treated samples. Higher treatment temperature (200 °C) increased wood elasticity in compression in all the anatomical directions despite wood moisture content during the measurements. Multivariate analysis revealed that the modification temperature significantly affected the modulus of elasticity perpendicular to the grain, while in the case of compression strength, the statistically significant effect was observed only parallel to the grain. The results obtained can be useful from an industrial perspective and can serve as part of a database for further modelling purposes.