Low-intensity drying is widely believed to protect waterlogged archeological wood against the adverse effects of dimensional alteration and cracking. However, slow drying generates substantial costs for the conservation process. This study compares the effects on conservation of highly-degraded sapwood (SW) and slightly-degraded heartwood (HW) from waterlogged archeological Scots pine wood treated with polyethylene glycol either as a mixture of polyethylene glycol (PEG) 400/4000 or PEG 2000 solution and air-dried using different approaches. The reference air-drying approach, using gradually decreasing air relative humidity (RH), i.e., 96, 86, 75, 66, and finally 44% (multi-stage schedule), was compared to an alternative approach, using constant RH of 44% (single-stage schedule). The Fourier-transform infrared spectroscopy (FTIR) analysis confirmed the decomposition of hydrophilic chemical wood components and revealed differences in the degree of degradation of waterlogged SW and HW. The drying time of PEG-treated waterlogged wood air-dried using a one-stage schedule was shorter compared to the drying time using multi-stage drying. Multivariate analysis (ANOVA) revealed that the drying schedule used after impregnation of waterlogged wood with PEG can have a beneficial effect on wood hygroscopicity and dimensional stability. The drying schedule significantly affected the equilibrium moisture content (EMC) of SW and HW and reduced tangential (S_T) shrinkage of SW. These results show the positive effect of the single-stage alternative drying approach on the dimensional stability of highly-degraded Scots pine SW impregnated with PEG 2000. In the case of slightly-degraded HW, the drying approach did not affect wood preservation. These results can be useful for the conservation of highly-degraded waterlogged Scots pine wood.

The aim of the present work was to test the applicability of the spectrophotometric method for the determination of polyethylene glycol (PEG) 4000 using bismuth subnitrate (BiONO₃) to monitor the content of PEG in impregnated archaeological wood. Absorption spectra were collected in the visible light (VIS) range from 400 to 600 nm. The weight of the wood samples tested ranged from 50 to 120 mg. The PEG content was measured in aqueous extracts with the concentration of up to 30 mg·L⁻¹. The results confirmed the high sensitivity and precision of the method used. The performed analyses were characterized by repeatability and selectivity towards PEG 4000 in a mixture containing PEG 300. The applicability of the PEG 2000 quantitative determination method was confirmed.

Environmental conditions present in mines generally are very favourable to decay; high temperature, high humidity, variable oxygen content, numerous metal-wood connections and the presence of a high content of inorganic compounds typical of mines have a significant impact on the biotic and abiotic degradation factors. The state of conservation of wooden artefacts from the Złoty Stok (Poland) gold mine was investigated using a multi-analytical approach. The aim was to select the conservation treatments that would stop decay and improve the conditions and dimensional stability of the wood. FT-IR and Py-GC/MS were used to assess the state of preservation of lignocellulosic material. ED-XRF and SEM-EDS were used to determine—and XRD to identify crystalline phases—salts and minerals in the wood structure or efflorescence on the surface. Highly degraded lignocellulosic material that had undergone depolymerisation and oxidation was found to be severely contaminated by iron-based mineral substances, mainly pyrite, and in some cases greigite and magnetite. The presence of inorganic salts made it difficult to choose the best consolidating material to reduce the level of decay and improve the dimensional stability of the wood.