Magnetic iron oxide-silica shell nanocomposites with different iron oxide/silica ratio were synthesized and structurally characterized by Fourier transform infrared (FT-IR) spectroscopy, X-ray diffraction (XRD), small-angle neutron scattering, magnetic and N₂-sorption studies. The composite that resulted with the best properties in terms of contact surface area and saturation of magnetization was selected for Pb²⁺ adsorption studies from aqueous media. The material presented good absorption capacity (maximum adsorption capacity 14.9 mg·g⁻¹) comparable with similar materials presented in literature. Its chemico-physical stability and adsorption capacity recommend the nanocomposite as a cheap adsorbent material for lead.

This study aims to remove arsenic from an aqueous medium by adsorption on a nanocomposite material obtained by the sol–gel method starting from matrices of silica, iron oxide and NaF (SiO₂/Fe(acac)₃/NaF). Initially, the study focused on the synthesis and characterization of the material by physico–chemical methods such as: X-ray diffraction, FT-IR spectroscopy, Raman spectroscopy, atomic force microscopy, and magnetization. Textural properties were obtained using nitrogen adsorption/desorption measurements. The zero load point, pHpZc, was also determined by the method of bringing the studied system into equilibrium. In addition, this study also provides a comprehensive discussion of the mechanism of arsenic adsorption by conducting kinetic, thermodynamic and equilibrium studies. Studies have been performed to determine the effects of adsorbent dose, pH and initial concentration of arsenic solution, material/arsenic contact time and temperature on adsorption capacity and material efficiency. Three theoretical adsorption isotherms were used, namely Langmuir, Freundlich and Sips, to describe the experimental results. The Sips isotherm was found to best describe the experimental data obtained, the maximum adsorption capacity being ~575 µg As(III)/g. The adsorption process was best described by pseudo-second order kinetics. Studies have been performed at different pH values to establish not only the optimal pH at which the adsorption capacity is maximum, but also which is the predominantly adsorbed species. The effect of pH and desorption studies have shown that ion exchange and the physiosorption mechanism are implicated in the adsorption process. From a thermodynamic point of view, parameters such as ΔG°, ΔH° and ΔS° were evaluated to establish the mechanism of the adsorption process. Desorption studies have been performed to determine the efficiency of the material and it has been shown that the material can be used successfully to treat a real-world example of deep water with a high arsenic content.

The adsorptive potential has been evaluated for the aminopropyl functionalized mesoporous silica materials obtained by co-condensation and post grafting methods. Nitrogen sorption, small angle neutron and X-ray scattering (SANS and SAXS) demonstrated high surface area and well-ordered hexagonal pore structure suitable for applications as adsorbents of metals from waste waters. A comparison of Cr(VI) adsorption properties of the materials prepared by different functionalization methods has been performed. The obtained results demonstrated the adsorption capacity due to the affinity of the chromium ions to the amino groups, and showed that co-condensation of tetraethoxysilane (TEOS) and 3-aminopropyl triethoxysilane (APTES) resulted in higher metal sorption capacity of the materials compared to post-synthesis grafting of aminopropyl groups onto the mesoporous silica particles.

Mesoporous silica particles have been prepared with functionalized precursors, used either in situ co-condensation process or as post-synthesis grafting agents, in order to deliver surface functionalisation. Aminopropyl, mercaptopropyl, vinyl and hexyl organosilanes were used as funtionalized precursors, tetraethylorthosilicat as the base silica precursor material, hexadecyl-trimethylammonium bromide (CTAB) as directing agent and water-ethanol mixture as solvent, with ammonia catalyst. The aim was to explore the effect of various recipes on the structural properties of the composite materials. The samples’ microstructures have been evaluated using nitrogen sorption and small angle neutron scattering. Ordered mesoporous structures were obtained, for almost all synthesis conditions, after the solvent-extraction of the template agent. Only in one case, for the materials functionalized by mercaptopropyl groups in co-condensation route, disordered amorphous structure was obtained. All samples functionalized by post-grafting presented well-ordered structures mesoporous structures. The results have potential use for easy design of sorbent materials for drug loading or pollutant adsorption applications.