Polyvinylidene fluoride (PVDF)-based piezoelectric materials (PEMs) have found extensive applications in energy harvesting which are being extended consistently to diverse fields requiring strenuous service conditions. Hence, there is a pressing need to mass produce PVDF-based PEMs with the highest possible energy harvesting ability under a given set of conditions. To achieve high yield and efficiency, solution blow spinning (SBS) technique is attracting a lot of interest due to its operational simplicity and high throughput. SBS is arguably still in its infancy when the objective is to mass produce high efficiency PVDF-based PEMs. Therefore, a deeper understanding of the critical parameters regarding design and processing of SBS is essential. The key objective of this review is to critically analyze the key aspects of SBS to produce high efficiency PVDF-based PEMs. As piezoelectric properties of neat PVDF are not intrinsically much significant, various additives are commonly incorporated to enhance its piezoelectricity. Therefore, PVDF-based copolymers and nanocomposites are also included in this review. We discuss both theoretical and experimental results regarding SBS process parameters such as solvents, dissolution methods, feed rate, viscosity, air pressure and velocity, and nozzle design. Morphological features and mechanical properties of PVDF-based nanofibers were also discussed and important applications have been presented. For completeness, key findings from electrospinning were also included. At the end, some insights are given to better direct the efforts in the field of PVDF-based PEMs using SBS technique.

This paper introduces a new usage of piezoelectric poly (vinylidene fluoride) (PVDF) electrospun nanofiber (NF) membrane as a sensing unit for acoustic signals. In this work, an NF mat has been used as a transducer to convert acoustic signals into electric voltage outcomes. The detected voltage has been analyzed as a function of both frequency and amplitude of the excitation acoustic signal. Additionally, the detected AC signal can be retraced as a function of both frequency and amplitude with some wave distortion at relatively higher amplitudes and within a certain acoustic spectrum region. Meanwhile, the NFs have been characterized through piezoelectric responses, beta sheet calculations and surface morphology. This work is promising as a low-cost and innovative solution to harvest acoustic signals coming from wide resources of sound and noise.

Carbon nanotubes (CNTs) are a robust material and proven as a promising candidate for a wide range of electronic, optoelectronic and environmental applications. In this work, two different methods were utilized for the preparation of CNTs exhibiting different aspect ratios via chemical vapor deposition (CVD). The as-prepared CNTs were analyzed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), N₂adsorption isotherms, thermogravimetric analysis and Raman spectroscopy in order to investigate their morphological and structural properties. Free-standing CNTs “buckypaper” membranes were fabricated, characterized and tailored to meet the requirements of two applications, i.e., (1) the removal of humic acid (HA) from water and (2) separation of oil-in-water emulsions. It was revealed that the hydrophobic buckypapers showed high separation performance for Shell oil-in-water emulsions filtration, with up to 98% through the accumulation of oil droplets onto the membrane surface. The absorption capacity of buckypaper membranes for various organic liquids (oil, chloroform and toluene) was evaluated over 10 absorption cycles to investigate their recyclability and robustness. Moreover, surface modification was introduced to the pristine CNTs to increase their surface hydrophilicity and improve the pure water permeability of buckypapers. These modified buckypapers showed high flux for HA solutions and excellent HA rejection efficiency up to 95%via size exclusion and electrostatic repulsion mechanisms.

Computational fluid dynamics (CFD) was used to investigate characteristics of high-speed air as it is expelled from a solution blow spinning (SBS) nozzle using a k-ε turbulence model. Air velocity, pressure, temperature, turbulent kinetic energy and density contours were generated and analysed in order to achieve an optimal attenuation force for fibre production. A bespoke convergent nozzle was used to produce polyvinylidene fluoride (PVDF) fibres at air pressures between 1 and 5 bar. The nozzle comprised of four parts: a polymer solution syringe holder, an air inlet, an air chamber, and a cap that covers the air chamber. A custom-built SBS setup was used to produce PVDF submicron fibres which were consequently analysed using scanning electron microscope (SEM) for their morphological features. Both theoretical and experimental observations showed that a higher air pressure (4 bar) is more suitable to achieve thin fibres of PVDF. However, fibre diameter increased at 5 bar and intertwined ropes of fibres were also observed.

Solution blow spinning (SBS) is gaining popularity for producing fibres for smart textiles and energy harvesting due to its operational simplicity and high throughput. The whole SBS process is significantly dependent on the characteristics of the attenuation force, i.e., compressed air. Although variation in the fibre morphology with varying air input pressure has been widely investigated, there is no available literature on the experimentally determined flow characteristics. Here, we have experimentally measured and calculated airflow parameters, namely, output air pressure and velocity in the nozzle wake at 12 different pressure values between 1 and 6 bar and 11 different positions (retracted 5 mm to 30 mm) along the centreline. The results obtained in this work will answer many critical questions about optimum protrusion length for the polymer solution syringe and approximate mean fibre diameter for polyvinylidene fluoride (PVDF) at given output air pressure and velocity. The highest output air pressure and velocity were achieved at a distance of 3–5 mm away from the nozzle wake and should be an ideal location for the apex of the polymer solution syringe. We achieved 250 nm PVDF fibres when output air pressure and velocity were 123 kPa and 387 m/s, respectively.