In this paper, the influence of bentonite (BNT) on rheological properties, linear shrinkage, hardness, and structure of polyethylene wax (PE-wax) used in the lost-wax casting process are studied. Experiments were conducted with PE-wax with different contents of bentonite (from 0.1 to 5 wt.%). The structural changes of modified polyethylene wax were evaluated using differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). The addition of bentonite in a concentration range between 0 and 0.8 wt.% into PE-wax caused a decrease of the linear shrinkage and the hardness of PE-wax/BNT blends. Modified polyethylene wax containing greater than 1 wt.% of the filler showed an increase in viscosity. The DSC-based investigations confirmed good miscibility and a uniform structure of PE-wax with BNT. Moreover, an increase in melting temperature onset and its enthalpy observed for filler PE-wax material showed an influence of bentonite on the crystalline structure of the polymeric matrix. SEM observations of the fractured surfaces confirmed the homogeneous structure of blends with contents up to 0.8 wt.% BNT. In the case of higher filler concentrations, the presence of more numerous and large clusters of filler in the polymer matrix was observed due to the increase in the viscosity of the PE-wax/BNT melt composition during mixing. The PE-wax blend with 0.4 wt.% BNT gives better results of reduced linear shrinkage and lower hardness than unmodified material. Lastly, a new developed material (PE-wax/0.4 BNT) was subjected to technological tests, consisting of the preparation of the mold and manufacture of a high-quality aluminum cast, using the lost-wax method.

This paper presented a new approach to decision making support of defects assessment in metal matrix composites (MMC). It is a continuation of the authors’ papers in terms of a uniform method of casting defects assessment. The idea of this paper was to design an open-access application (follow-up system called Open Atlas of Casting Defects (OACD)) in the area of industry and science. This a new solution makes it possible to quickly identify defect types considering the new classification of casting defects. This classification complements a classical approach by adding a casting defect group called structure defects, which is especially important for metal matrix composites. In the paper, an application structure, and the possibility of its use in casting defects assessment were introduced.

Investment casting is one of the precise casting methods where disposable wax patterns made in wax injection molds are used to make a casting mold. The production capacity of precision foundry is determined by the time taken for producing wax patterns, which depends on the time taken for wax solidification. Wax injection molds are usually made of aluminum or copper alloys with the use of expensive and time-consuming computer numerical control (CNC) processing, which makes low-volume production unprofitable. To reduce these costs, the authors present a heat transfer analysis of a 3D printed wax injection mold. Due to the low thermal conductivity of the photopolymer resin, the influence of different cooling channels’ shapes was investigated to improve the time of the manufacturing process. Transient thermal analysis was performed using COMSOL software based on the finite element method (FEM) and included a simulation of wax injection mold cooling with cold air (−23 °C), water, and without cooling. The analysis showed that use of cooling channels in the case of photopolymer material significantly reduces the solidification time of the sample (about 10 s shorter), and that under certain conditions, it is possible to obtain better cooling than obtained with the aluminum reference wax injection mold (after approximately 25–30 s). This approach allows to reduce the production costs of low-volume castings.

The investment casting method supported with 3D-printing technology, allows the production of unit castings or prototypes with properties most similar to those of final products. Due to the complexity of the process, it is very important to control the dimensions in the initial stages of the process. This paper presents a comparison of non-contact measurement systems applied for testing of photopolymer 3D-printed injection die used in investment casting. Due to the required high quality of the surface parameters, the authors decided to use the DPP (Daylight Polymer Printing) 3D-printing technology to produce an analyzed injection die. The X-ray CT, Structured blue-light scanner and focus variation microscope measurement techniques were used to avoid any additional damages to the injection die that may arise during the measurement. The main objective of the research was to analyze the possibility of using non-contact measurement systems as a tool for analyzing the quality of the surface of a 3D-printed injection die. Dimensional accuracy analysis, form and position deviations, defect detection, and comparison with a CAD model were carried out.

ZnO thin layers were deposited on p-type silicon substrates by the sol-gel spin-coating method and, then, annealed at various temperatures in the range of 573–873 K. Photoluminescence was carried out in the temperature range of 20–300 K. All samples showed two dominant peaks that have UV emissions from 300 nm to 400 nm and visible emissions from 400 nm to 800 nm. Influence of temperature on morphology and chemical composition of fabricated thin layers was examined by XRD, SEM, FTIR, and Raman spectroscopy. These measurements indicate that ZnO structure is obtained for samples annealed at temperatures above 573 K. It means that below this temperature, the obtained thin films are not pure zinc oxide. Thus, annealing temperature significantly affected crystallinity of the thin films.