There is a strong demand for materials with inherently high creep resistance in the harsh environment of next-generation nuclear reactors. High entropy alloys have drawn intense attention in this regard due to their excellent elevated temperature properties and irradiation resistance. Here, the time-dependent plastic deformation behavior of two refractory high entropy alloys was investigated, namely HfTaTiVZr and TaTiVWZr. These alloys are based on reduced activity metals from the 4-5-6 elemental palette that would allow easy post-service recycling after use in nuclear reactors. The creep behavior was investigated using nano-indentation over the temperature range of 298 K to 573 K under static and dynamic loads up to 5 N. Creep stress exponent for HfTaTiVZr and TaTiVWZr was found to be in the range of 20–140 and the activation volume was ~16–20b³, indicating dislocation dominated mechanism. The stress exponent increased with increasing indentation depth due to a higher density of dislocations and their entanglement at larger depth and the exponent decreased with increasing temperature due to thermally activated dislocations. Smaller creep displacement and higher activation energy for the two high entropy alloys indicate superior creep resistance compared to refractory pure metals like tungsten.

Lamellar eutectic structure in Al_0.7CoCrFeNi high-entropy alloy (HEA) is emerging as a promising candidate for structural applications because of its high strength-ductility combination. The alloy consists of a fine-scale lamellar fcc + B2 microstructure with high flow stresses > 1300 MPa under quasi-static tensile deformation and >10% ductility. The response to shear loading was not investigated so far. This is the first report on the shear deformation of a eutectic structured HEA and effect of precipitation on shear deformation. A split-Hopkinson pressure bar (SHPB) was used to compress the hat-shaped specimens to study the local dynamic shear response of the alloy. The change in the width of shear bands with respect to precipitation and deformation rates was studied. The precipitation of L1₂ phase did not delay the formation of adiabatic shear bands (ASB) or affect the ASB width significantly, however, the deformed region around ASB, consisting of high density of twins in fcc phase, was reduced from 80 µm to 20 µm in the stronger precipitation strengthened condition. We observe dynamic recrystallization of grains within ASBs and local mechanical response of individual eutectic lamellae before and after shear deformation and within the shear bands was examined using nano-indentation.

Refractory high-entropy alloys (RHEAs) have recently attracted widespread attention due to their outstanding mechanical properties at elevated temperatures, making them appealing for concentrating solar power and nuclear energy applications. Here, the corrosion behavior of equimolar HfTaTiVZr and TaTiVWZr RHEAs was investigated in molten FLiNaK eutectic salt (LiF-NaF-KF: 46.5−11.5−42 mol.%) at 650 °C. Potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and immersion test measurements were carried out for these two RHEAs and compared with Inconel 718 (IN718) superalloy and SS316 stainless steel under identical test conditions. Both TaTiVWZr and HfTaTiVZr refractory high-entropy alloys exhibited an order of magnitude lower corrosion rate than SS316. IN718 and TaTiVWZr showed similar corrosion rates. Corrosion products enriched with noble alloying elements formed in the case of TaTiVWZr and IN718 were stable and protective on the substrate. SS316 showed the lowest corrosion resistance and void formation along the exposed surface due to the active dissolution of Cr and Fe, which provided diffusion paths for the corroded species. The surface analysis results showed that IN718 underwent pitting corrosion, while TaTiVWZr experienced selective dissolution in the inter-dendritic area. In contrast, HfTaTiVZr and SS316 experienced corrosion at the grain boundaries.