There has been tremendous interest in recent years in a new class of multi-component metallic alloys that are referred to as high entropy alloys, or more generally, as complex concentrated alloys. These multi-principal element alloys represent a new paradigm in structural material design, where numerous desirable attributes are achieved simultaneously from multiple elements in equimolar (or near equimolar) proportions. While there are several review articles on alloy development, microstructure, mechanical behavior, and other bulk properties of these alloys, then there is a pressing need for an overview that is focused on their surface properties and surface degradation mechanisms. In this paper, we present a comprehensive view on corrosion, erosion and wear behavior of complex concentrated alloys. The effect of alloying elements, microstructure, and processing methods on the surface degradation behavior are analyzed and discussed in detail. We identify critical knowledge gaps in individual reports and highlight the underlying mechanisms and synergy between the different degradation routes.

Eutectic high entropy alloys, with lamellar arrangement of solid solution phases, represent a new paradigm for simultaneously achieving high strength and ductility, thereby circumventing this well-known trade-off in conventional alloys. However, dynamic strengthening mechanisms and phase-boundary interactions during external loading remain unclear for these eutectic systems. In this study, small-scale mechanical behavior was evaluated for AlCoCrFeNi_2.1 eutectic high entropy alloy, consisting of a lamellar arrangement of L1₂ and B2 solid-solution phases. The ultimate tensile strength was 1165 MPa with ductility of ~18% and ultimate compressive strength was 1863 MPa with a total compressive fracture strain of ~34%. Dual mode fracture was observed with ductile failure for L1₂ phase and brittle mode for B2 phase. Phase-specific mechanical tests using nano-indentation and micro-pillar compression showed higher hardness and strength and larger strain rate sensitivity for B2 compared with L1₂. Micro-pillars on B2 phase deformed by plastic barreling while L1₂ micro-pillars showed high density of slip steps due to activation of more slip systems and homogenous plastic flow. Mixed micro-pillars containing both the phases exhibited dual yielding behavior while the interface between L1₂ and B2 was well preserved without any sign of separation or cracking. Phase-specific friction analysis revealed higher coefficient of friction for B2 compared to L1₂. These results will pave the way for fundamental understanding of phase-specific contribution to bulk mechanical response of concentrated alloys and help in designing structural materials with high fracture toughness.

CoCrFeMnNi high entropy alloys (HEAs) were additively manufactured (AM) by laser powder bed fusion and their corrosion resistance in 3.5 wt% NaCl solution was studied by potentiodynamic polarization and electrochemical impedance spectroscopy tests. A systematic study of AM CoCrFeMnNi HEAs’ porosity under a wide range of laser processing parameters was conducted and a processing map was constructed to identify the optimal laser processing window for CoCrFeMnNi HEAs. The near fully dense AM CoCrFeMnNi HEAs exhibit a unique non-equilibrium microstructure consisting of tortuous grain boundaries, sub-grain cellular structures, columnar dendrites, associated with some processing defects such as micro-pores. Compared with conventional as-cast counterpart, the AM CoCrFeMnNi HEAs showed higher pitting resistance (ΔE) and greater polarization resistance (R_p). The superior corrosion resistance of AM CoCrFeMnNi HEAs may be attributed to the homogeneous elemental distribution and lower density of micro-pores. Our study widens the toolbox to manufacture HEAs with exceptional corrosion resistance by additive manufacturing.