Measurements are carried out of the Barkhausen noise (BN) and hardness on specimens where changes in hardness were obtained due to strain hardening (S235 and DC01 steels) and due to thermochemical treatment (AMS 6414 steel). A method is presented of processing the recorded BN signal to extract diagnostic information. The BN number of events is selected as the signal characteristic property to develop relevant correlations. A new methodology is presented for the development of correlations between the Barkhausen noise number of events and hardness. A possibility is indicated of developing correlations with a high R2 determination coefficient. The method limitations are specified.

The aim of this study was to investigate the effect of plasterboards’ humidity absorption on their performance. Specimens’ hydration procedure consisted of consecutive immersing in water and subsequent drying at room temperature. Such a procedure was performed to increase the content of moisture within the material volume. The microstructural observations of five different plasterboard types were performed through optical and scanning electron microscopy. The deterioration of their properties was evaluated by using a three-point bending test and a subsequent ultrasonic (ultrasound testing (UT)) longitudinal wave velocity measurement. Depending on the material porosity, a loss of UT wave velocity from 6% to 35% and a considerable decrease in material strength from 70% to 80% were observed. Four types of approximated formulae were proposed to describe the dependence of UT wave velocity on board moisture content. It was found that the proposed UT method could be successfully used for the on-site monitoring of plasterboards’ hydration processes.

This paper presents the possibility of using low-module polypropylene dispersed reinforcement (E = 4.9 GPa) to influence the load-deflection correlation of cement composites. Problems have been indicated regarding the improvement of elastic range by using that type of fibre as compared with a composite without reinforcement. It was demonstrated that it was possible to increase the ability to carry stress in the Hooke’s law proportionality range in mortar and paste types of composites reinforced with low-module fibres, i.e., V_f = 3% (in contrast to concrete composites). The possibility of having good strengthening and deflection control in order to limit the catastrophic destruction process was confirmed. In this paper, we identify the problem of deformation assessment in composites with significant deformation capacity. Determining the effects of reinforcement based on a comparison with a composite without fibres is suggested as a reasonable approach as it enables the comparison of results obtained by various universities with different research conditions.

This study presents a novel approach for the non-destructive evaluation of hardness in S235JR ferromagnetic steel using low-frequency impedance spectroscopy combined with advanced multivariate statistical analysis. The primary objective was to develop a correlation model enabling estimation of...