The thermocatalytic hydrogenation of carbon dioxide (CO₂) to methanol is considered as a potential route for green hydrogen storage as well as a mean for utilizing captured CO₂, owing to the many established applications of methanol. Copper–zinc bimetallic catalysts supported on a zirconium-based UiO-66 metal–organic framework (MOF) were prepared via slurry phase impregnation and benchmarked against the promoted, co-precipitated, conventional ternary CuO/ZnO/Al₂O₃ (CZA) catalyst for the thermocatalytic hydrogenation of CO₂ to methanol. A decrease in crystallinity and specific surface area of the UiO-66 support was observed using X-ray diffraction and N₂-sorption isotherms, whereas hydrogen-temperature-programmed reduction and X-ray photoelectron spectroscopy revealed the presence of copper active sites after impregnation and thermal activation. Other characterisation techniques such as scanning electron microscopy, transmission electron microscopy, and thermogravimetric analysis were employed to assess the physicochemical properties of the resulting catalysts. The UiO-66 (Zr) MOF-supported catalyst exhibited a good CO₂ conversion of 27 and 16% selectivity towards methanol, whereas the magnesium-promoted CZA catalyst had a CO₂ conversion of 31% and methanol selectivity of 24%. The prepared catalysts performed similarly to a CZA commercial catalyst which exhibited a CO₂ conversion and methanol selectivity of 30 and 15%. The study demonstrates the prospective use of Cu-Zn bimetallic catalysts supported on MOFs for direct CO₂ hydrogenation to produce green methanol.

Waste plastics such as polyethylene terephthalate (w-PET) and stockpiled discard coal (d-coal) pose a global environmental threat as they are disposed of in large quantities as solid waste into landfills and are particularly hazardous due to spontaneous combustion of d-coal that produces greenhouse gases (GHG) and the non-biodegradability of w-PET plastic products. This study reports on the development of a composite material, prepared from w-PET and d-coal, with physical and chemical properties similar to that of metallurgical coke. The w-PET/d-coal composite was synthesized via a co-carbonization process at 700 °C under a constant flow of nitrogen gas. Proximate analysis results showed that a carbonized w-PET/d-coal composite could attain up to 35% improvement in fixed carbon content compared to its d-coal counterpart, such that an initial fixed carbon content of 14–75% in carbonized discard coal could be improved to 49–86% in carbonized w-PET/d-coal composites. The results clearly demonstrate the role of d-coal ash on the degree of thermo-catalytic conversion of w-PET to solid carbon, showing that the yield of carbon derived from w-PET (i.e., c-PET) was proportional to the ash content of d-coal. Furthermore, the chemical and physical characterization of the composition and structure of the c-PET/d-coal composite showed evidence of mainly graphitized carbon and a post-carbonization caking ability similar to that of metallurgical coke. The results obtained in this study show potential for the use of waste raw materials, w-PET and d-coal, towards the development of an eco-friendly reductant with comparable chemical and physical properties to metallurgical coke.