The embrittlement of two types of nuclear pressure vessel steel, 15Kh2NMFA and A508 Cl.2, was studied using two different methods of magnetic nondestructive testing: micromagnetic multiparameter microstructure and stress analysis (3MA-X8) and magnetic adaptive testing (MAT). The microstructure and mechanical properties of reactor pressure vessel (RPV) materials are modified due to neutron irradiation; this material degradation can be characterized using magnetic methods. For the first time, the progressive change in material properties due to neutron irradiation was investigated on the same specimens, before and after neutron irradiation. A correlation was found between magnetic characteristics and neutron-irradiation-induced damage, regardless of the type of material or the applied measurement technique. The results of the individual micromagnetic measurements proved their suitability for characterizing the degradation of RPV steel caused by simulated operating conditions. A calibration/training procedure was applied on the merged outcome of both testing methods, producing excellent results in predicting transition temperature, yield strength, and mechanical hardness for both materials.

The neutron irradiation embrittlement of four different types of nuclear pressure vessel materials (three base metals and one weld material) were investigated by a magnetic nondestructive testing method, magnetic adaptive testing (MAT). The method is based on the measurement of minor magnetic hysteresis loops on Charpy specimens irradiated by neutrons in the BR2 reactor. Due to the neutron irradiation, the structure of the material was modified. The Charpy impact method is suitable for destructive characterization of material embrittlement. The results of Charpy impact test measurements at SCK CEN Belgian Nuclear Research Centre were compared with the nondestructively measured magnetic parameters. A definite correlation was found between magnetic descriptors and the ductile-to-brittle transition temperature (DBTT), regardless of the type of material or irradiation condition. The results suggest that this “calibration curve“ can be used to estimate the DBTT from non-destructive measurements.

Nondestructive magnetic measurement methods can be successfully applied to determine the embrittlement of nuclear pressure vessel steel caused by neutron irradiation. It was found in previous works that reasonable correlation could be obtained between the nondestructively measured magnetic parameters and destructively determined ductile-to-brittle transition temperature. However, a large scatter of the measurement points was detected even in the cases of the non-irradiated reference samples. The reason for their scattering was attributed to the local inhomogeneity of material. This conclusion is verified in the present work by applying three different magnetic methods on two sets of Charpy samples made of two different reactor steel materials. It was found that by an optimal magnetic pre-selection of samples, a good, linear correlation can be found between magnetic parameters as well as the ductile-to-brittle transition temperature with low scattering of points. This result shows that neutron irradiation embrittlement depends very much on the local material properties.

During neutron irradiation of metals, owing to the enhanced number of vacancies and interstitial atoms, the climb motion of dislocations becomes significant at room temperature, leading to a recrystallization of the material. Moreover, the vacancies and interstitial atoms tend to form prismatic dislocation loops that play a crucial role in the plastic properties of the materials. X-ray peak profile analysis is an efficient nondestructive method to determine the properties of dislocation microstructure. In the first half of this article, the foundation of the asymptotic peak broadening theory and the related restricted-moments peak-evaluation method is summarized. After this, the microstructural parameters obtained by X-ray peak profile analysis are reported for irradiated E110 and E110G Zr alloys used as cladding material in the nuclear industry.

Neutron irradiation-generated embrittlement of nuclear pressure vessel steel was inspected by a nondestructive magnetic method, called magnetic adaptive testing (MAT). This method is based on systematic measurement and evaluation of minor magnetic hysteresis loops. Result of MAT measurement was compared with the result of the traditional Charpy measurement. Good correlation was found between these parameters. One of the main findings of the present work is that the considerable part of scatter of points obtained by magnetic measurement can be attributed to local material inhomogeneity. Another important conclusion is that the embrittlement highly depends on the initial local material conditions, i.e., the initial microstructure, which are very different even within the same block of reactor steel material. By taking this into account, the magnetic descriptors obtain more precise determination of the local embrittlement than the traditionally used destructive mechanical parameters from Charpy data.

Degradation of nuclear pressure vessel steel materials, 15Kh2NMFA type and A508 Cl2 type (definition is given in the text) were investigated by a novel magnetic nondestructive testing method, so-called Magnetic Adaptive Testing (MAT), which is based on systematic measurement and evaluation of minor magnetic hysteresis loops. The measured samples were thermally treated by a special step cooling procedure, which generated structural changes in the material. It was found that this type of degradation can be easily followed by magnetic measurements. Charpy impact test were also performed and the results were compared with the magnetic parameters. In case of 15Kh2NMFA steel, a good, reliable and closely linear correlation was found between magnetic descriptors and transition temperature.