The neutron irradiation embrittlement of four different types of nuclear pressure vessel materials (three base metals and one weld material) were investigated by a magnetic nondestructive testing method, magnetic adaptive testing (MAT). The method is based on the measurement of minor magnetic hysteresis loops on Charpy specimens irradiated by neutrons in the BR2 reactor. Due to the neutron irradiation, the structure of the material was modified. The Charpy impact method is suitable for destructive characterization of material embrittlement. The results of Charpy impact test measurements at SCK CEN Belgian Nuclear Research Centre were compared with the nondestructively measured magnetic parameters. A definite correlation was found between magnetic descriptors and the ductile-to-brittle transition temperature (DBTT), regardless of the type of material or irradiation condition. The results suggest that this “calibration curve“ can be used to estimate the DBTT from non-destructive measurements.

Degradation of nuclear pressure vessel steel materials, 15Kh2NMFA type and A508 Cl2 type (definition is given in the text) were investigated by a novel magnetic nondestructive testing method, so-called Magnetic Adaptive Testing (MAT), which is based on systematic measurement and evaluation of minor magnetic hysteresis loops. The measured samples were thermally treated by a special step cooling procedure, which generated structural changes in the material. It was found that this type of degradation can be easily followed by magnetic measurements. Charpy impact test were also performed and the results were compared with the magnetic parameters. In case of 15Kh2NMFA steel, a good, reliable and closely linear correlation was found between magnetic descriptors and transition temperature.