The embrittlement of two types of nuclear pressure vessel steel, 15Kh2NMFA and A508 Cl.2, was studied using two different methods of magnetic nondestructive testing: micromagnetic multiparameter microstructure and stress analysis (3MA-X8) and magnetic adaptive testing (MAT). The microstructure and mechanical properties of reactor pressure vessel (RPV) materials are modified due to neutron irradiation; this material degradation can be characterized using magnetic methods. For the first time, the progressive change in material properties due to neutron irradiation was investigated on the same specimens, before and after neutron irradiation. A correlation was found between magnetic characteristics and neutron-irradiation-induced damage, regardless of the type of material or the applied measurement technique. The results of the individual micromagnetic measurements proved their suitability for characterizing the degradation of RPV steel caused by simulated operating conditions. A calibration/training procedure was applied on the merged outcome of both testing methods, producing excellent results in predicting transition temperature, yield strength, and mechanical hardness for both materials.

The neutron irradiation embrittlement of four different types of nuclear pressure vessel materials (three base metals and one weld material) were investigated by a magnetic nondestructive testing method, magnetic adaptive testing (MAT). The method is based on the measurement of minor magnetic hysteresis loops on Charpy specimens irradiated by neutrons in the BR2 reactor. Due to the neutron irradiation, the structure of the material was modified. The Charpy impact method is suitable for destructive characterization of material embrittlement. The results of Charpy impact test measurements at SCK CEN Belgian Nuclear Research Centre were compared with the nondestructively measured magnetic parameters. A definite correlation was found between magnetic descriptors and the ductile-to-brittle transition temperature (DBTT), regardless of the type of material or irradiation condition. The results suggest that this “calibration curve“ can be used to estimate the DBTT from non-destructive measurements.

The nondestructive determination of the neutron-irradiation-induced embrittlement of nuclear reactor pressure-vessel steel is a very important and recent problem. Within the scope of the so-called NOMAD project funded by the Euratom research and training program, novel nondestructive electromagnetic testing and evaluation (NDE) methods were applied to the inspection of irradiated reactor pressure-vessel steel. In this review, the most important results of this project are summarized. Different methods were used and compared with each other. The measurement results were compared with the destructively determined ductile-to-brittle transition temperature (DBTT) values. Three magnetic methods, 3MA (micromagnetic, multiparameter, microstructure and stress analysis), MAT (magnetic adaptive testing), and Barkhausen noise technique (MBN), were found to be the most promising techniques. The results of these methods were in good agreement with each other. A good correlation was found between the magnetic parameters and the DBTT values. The basic idea of the NOMAD project is to use a multi-method/multi-parameter approach and to focus on the synergies that allow us to recognize the side effects, therefore suppressing them at the same time. Different types of machine-learning (ML) algorithms were tested in a competitive manner, and their performances were evaluated. The important outcome of the ML technique is that not only one but several different ML techniques could reach the required precision and reliability, i.e., keeping the DBTT prediction error lower than a ±25 °C threshold, which was previously not possible for any of the NDE methods as single entities. A calibration/training procedure was carried out on the merged outcome of the testing methods with excellent results to predict the transition temperature, yield strength, and mechanical hardness for all investigated materials. Our results, achieved within the NOMAD project, can be useful for the future potential introduction of this (and, in general, any) nondestructive evolution method.

The influence of surface roughness on magnetic measurements of Reactor Pressure Vessel Steels was investigated by applying two types of magnetic, non-destructive measurement on nuclear reactor pressure vessel steel samples: magnetic adaptive testing (MAT) and magnetic Barkhausen noise measurement (MBN). The surface roughness was modified by primary and secondary machine cutting forces. Different settings of machine cutting produced different surface conditions. It was found that for both measurements a monotonic correlation was found to exist between magnetic parameters and surface roughness. Results of the MAT measurements found that the correlation depends on the speed (i.e., on the applied slew rate) of the magnetizing current. In a similar fashion, results from the MBN method show good agreement with MAT, where the response diminishes with an increase in surface roughness. The results show the importance of accounting for surface condition in the interpretation of results of non-destructive magnetic testing.