The influence of grinding aids (pure triethanolamine and ethylene glycol) on the properties of cements, their compatibility with an acrylate-based superplasticizer and the rheological parameters of mortars were investigated. The presence of surfactants influences the standard properties of cements and the effectiveness of the superplasticizer. The results of the heat of hydration and setting time measurements indicate a delay in the hydration process and an increase in the induction period duration of the surfactant-doped pastes, in relation to the reference sample without grinding aids. Triethanolamine increases early-age compressive strength; the effect was observed for both standard and superplasticizer-containing mortars. The presence of grinding aids decreases the slump flow of mortars and increases rheological parameters such as yield stress (τ₀) and viscosity (η).

The self-sealing process, associated with chemical and microstructural changes inside damaged cement-based composites, leads to the recovery of the original material integrity. Assessing the magnitude of internal changes in samples using non-destructive techniques to capture only the self-sealing effects is difficult. The challenge is evaluating the differences between subsequent observations in time and between samples with different properties. This paper proposes a new approach to the use of an ultrasonic technique for self-sealing investigation. The method allows the quantification of material changes strictly related to self-sealing processes, excluding changes caused by the naturally progressing hydration of binders. The applied ultrasonic pulse velocity (UPV) data processing procedure allows the investigation of material changes inside and near the cracks, the effects of stimulating the self-sealing of cement composites with mineral additives, and the assessment of changes over time. An important aspect of the method is the sample preparation procedure and testing conditions that reduce the impact of moisture content on the UPV measurements. New parameters allowing the quantitative characterization of the self-sealing process are proposed. The method was evaluated using cement mortars modified with siliceous fly ash with induced cracks 0 to 750 µm wide, which were then cured in water for 152 days. The maximum degree of effective crack filling as a result of autogenous self-sealing in the tested mortars was determined to range from 33% to 57%. Observations of the microstructure of the crack surface confirmed that apart from the volume of the newly formed products, the density of these products may have a key impact on the ultrasonic measurements of the self-sealing performance. The studies were supplemented by the examination of the compression strength of mortars, mortar sample scanning and computer image processing, and observations using an optical microscope and scanning electron microscope with energy dispersive spectroscopy.

Over the last 20 years, flue gas desulfurization gypsum (FGD gypsum) has become a valuable and widely used substitute for a natural raw material to produce plasters, mortars, and many other construction products. The essential advantages of FGD gypsum include its high purity and stability, which allow for better technical parameters compared to natural gypsum, and, until recently, its low price and easy availability. This FGD gypsum is obtained in the process of desulfurization of flue gases and waste gases in power plants, thermal power plants, refineries, etc., using fossil fuels such as coal or oil. The gradual reduction in energy production from fossil raw materials implemented by European Union countries until its complete cessation in 2049 in favor of renewable energy sources significantly affects the availability of synthetic gypsum, and forces producers of mortars and other construction products to look for new solutions. The gypsum content in commonly used light plaster mortars is usually from 50 to 60% by mass. This work presents the results of tests on mortars wherein the authors reduced the amount of gypsum to 30%, and, to meet the strength requirements specified in the EN 13279-1:2008 standard, added Portland cement in the amount of 6–12% by mass. Such a significant reduction in the content of synthetic gypsum will reduce this raw material’s consumption, thus extending its availability and developing other solutions. The study presented the test results on strength, density, porosity, pore size distribution, and changes in the microstructure of mortars during up to 180 days of maturation in conditions of increased relative humidity. The results show that decreased porosity and increased mechanical strength occur due to the densification of the microstructure caused by the formation of hydration products, such as C-S-H, ettringite, and thaumasite.

This paper aims to study the suitability of partial replacement of lime by waste originating from the cleaning of flue gases from the combustion of industrial wastes in the production of autoclaved aerated concrete (AAC). The compressive strength, bulk density, pore structure, phase composition, and microstructure of hydration products of the AAC were analyzed. According to the results, the addition of the waste can effectively enhance the mechanical properties of AAC due to the differences in morphology of hydration product—1.1 nm tobermorite and related dense microstructure. The pore size distribution was significantly influenced by waste addition, which was one of the main reasons for the increase in thermal conductivity. The XRD and SEM results showed that foreign ions introduced with the wastes affect the synthesis of 1.1 nm tobermorite. Moreover, it was shown that waste containing a high content of CaO can be used as lime replacement, which allows reducing CO₂ emissions during the AAC production process.

The introduction of the European Union’s climate change legislation and the intended use of renewable energy sources instead of fossil fuels will significantly reduce the production of flue gas desulfurization (FGD) gypsum used as the raw material for gypsum mortar plasters’ production. This has forced mortar producers to look for alternative materials, including gypsum–cement composites. This work investigated the mechanical strength and linear extension of four gypsum–cement mortars with the gypsum content reduced to 30%. The authors showed that the cement admixture of 6 to 12% introduced into the prepared mortars resulted in the formation of gypsum–cement mortars, which fulfill the requirements of the EN 13279-1:2008 standard concerning mechanical strength. This publication took into account the use of scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and X-ray diffractometry to characterize the chemical and phase composition of the mortars up to 180 days of dry air curing and increased relative humidity (RH) conditions. The formation of thaumasite, ettringite, and mixed ettringite–thaumasite phases was interesting because of their deleterious effect on the durability of plaster mortars.

Calcium aluminate cement (CAC) mortars and concrete may be used as high-performance repairing materials for pavement restoration in airfields and roads. During recent years alkali-silica reaction (ASR) was reported in Portland cement concrete subjected to the action of organic deicers. Present paper reports the results of the investigation on the influence of organic and inorganic alkali deicers on ASR potential in CAC mortars containing fused silica as model reactive aggregate. It was shown for the first time, that concentrated solutions of sodium and potassium acetates, as well as sodium chloride, can cause ASR in CAC mortars. Sodium and potassium acetate resulted in much larger expansions comparing to sodium chloride and sodium hydroxide solutions used as a reference. Differences in alkali-silica gel were found depending on the solution which samples were soaked in. It was shown that ASR could proceed in a system without calcium hydroxide and an external source of hydroxyl ions.