The goal of the presented work was to find the most favorable conditions for the synthesis and stabilization of chemically pure ettringite and monosulfate. The reaction was carried out by mixing pure tricalcium aluminate (C₃A) and gypsum (C$\overline{\mathrm{S}}$H₂) in an excess amount of water. The impact of hydration time (2–7 days), C₃A:C$\overline{\mathrm{S}}$ molar ratio (1:1–1:3) and water vapor pressure of the selected drying agents (anhydrite-III and supersaturated CaCl₂ solution) on the phase composition of the products was evaluated. After 7 days of hydration, either ettringite or monosulfate was obtained as the main product, depending on the C₃A:C$\overline{\mathrm{S}}$ molar ratio. The synthesis carried out at a C₃A:C$\overline{\mathrm{S}}$ molar ratio of 1:3 produced pure ettringite. In the case of the sample characterized by the ratio of 1:1 (typical of monosulfate), a considerable portion of ettringite (27.9%) was present in the final products along the AFm phase. Therefore, a different synthesis method has to be selected in order to obtain pure monosulfate. The results showed that thermal analysis, X-ray diffractometry and FTIR spectroscopy can be used to distinguish the characteristic features of ettringite and monosulfate.

The influence of four naturally occurring mineral additives (zeolite, diatomite, trass and bentonite) on the hydration and properties of cement pastes and mortars was investigated. The materials change the phase composition, heat of hydration (determined by calorimetry) and mechanical properties of composites. After 28 days, the amount of Ca(OH)₂ was reduced by up to 23% and up to 35% more C-S-H was formed, as proved by TG measurements. Differences were observed in the kinetics of heat release, especially for 25% of the addition. In the calorimetric curves, an additional exothermic effect is observed, related to the alteration in the hydration of C₃A in cement. From the point of view of beneficial influence on mechanical properties of mortars, the additives could be ranked as follows: bentonite < diatomite, zeolite < trass after 2 days and bentonite < diatomite < trass < zeolite after 28 days of curing. The highest compressive strength (58.5 MPa) was observed for the sample with a 10% addition of zeolite. Zeolite, trass, bentonite and diatomite are all pozzolanic materials; however, their activity varies to an extent due to the differences in their specific surface area and the content of the amorphous phase, responsible for the pozzolanic reaction.

The influence of grinding aids (pure triethanolamine and ethylene glycol) on the properties of cements, their compatibility with an acrylate-based superplasticizer and the rheological parameters of mortars were investigated. The presence of surfactants influences the standard properties of cements and the effectiveness of the superplasticizer. The results of the heat of hydration and setting time measurements indicate a delay in the hydration process and an increase in the induction period duration of the surfactant-doped pastes, in relation to the reference sample without grinding aids. Triethanolamine increases early-age compressive strength; the effect was observed for both standard and superplasticizer-containing mortars. The presence of grinding aids decreases the slump flow of mortars and increases rheological parameters such as yield stress (τ₀) and viscosity (η).