The production of stable and mature compost often depends on the performance of microbes and their enzymatic activity. Environmental and nutritional conditions influence the characteristics of microbial communities and, therefore, the dynamics of major metabolic activities. Using three waste mixtures (textile waste mixed with either green, paper, or cardboard waste), the maturity of the compost produced was assessed by following the physico-chemical parameters and enzymatic activities provided by the microorganisms that were identified using next-generation sequencing (NGS). Among the three mixtures used, it was found that the two best mixtures showed C/N ratios of 16.30 and 16.96, total nitrogen of 1.37 and 1.39%, cellulase activities of 50.62 and 52.67 Ug⁻¹, acid phosphatase activities of 38.81 and 68.77 Ug⁻¹, and alkaline phosphatase activities of 51.12 and 56.86 Ug⁻¹. In addition, several lignocellulosic species, together with those that are able to solubilize phosphate, were identified. Among those known for cellulase and acid/alkaline phosphatase activities, bacteria belonging to the Proteobacteria, Bacteroidetes, Actinobacteria, and Firmicutes phyla were shown. The presence of species belonging to the Ascomycota and Basidiomycota phyla of Fungi, which are known for their ability to produce cellulase and acid/alkaline phosphatases, was demonstrated. These findings provide a basis for the production of stable and mature compost based on textile waste.

In this study, tung tree and linseed drying oils, as well as semi-drying hempseed oil, were analyzed as the protective coatings for biocomposite boards (BcB) made of hemp shives, corn starch binder, and the performance-enhancing additives. The hydrophobization coatings were formed at 40, 90, and 120 °C temperatures, respectively. The physical-mechanical properties such as the compressive strength, thermal conductivity, dimensional stability, water absorption, and swelling were tested. In addition, scanning electron microscopy (SEM) was employed for the analysis of the board microstructure to visualize the oil fills and impregnation in pores and voids. It was demonstrated that the compressive strength of oil-modified BcBs compared to uncoated BcBs (at 10% of relative deformation) increased by up to 4.5-fold and could reach up to 14 MPa, water absorption decreased up to 4-fold (from 1.34 to 0.37 kg/m²), swelling decreased up to 48% (from 8.20% to 4.26%), whereas the thermal conductivity remained unchanged with the thermal conductivity coefficient of around 0.085 W/m·K. Significant performance-enhancing properties were obtained due to the formation of a protective oil film when the tung tree oil was used.