Hot electrons in semiconductors lose their energy very quickly (within picoseconds) to lattice vibrations. Slowing this energy loss could prove useful for more efficient photovoltaic or infrared devices. With their well-separated electronic states, quantum dots should display slow relaxation, but other mechanisms have made it difficult to observe. We report slow intraband relaxation (>1 nanosecond) in colloidal quantum dots. The small cadmium selenide (CdSe) dots, with an intraband energy separation of ∼0.25 electron volts, are capped by an epitaxial zinc selenide (ZnSe) shell. The shell is terminated by a CdSe passivating layer to remove electron traps and is covered by ligands of low infrared absorbance (alkane thiols) at the intraband energy. We found that relaxation is markedly slowed with increasing ZnSe shell thickness.

The intraband relaxation between the 1Pe and 1Se state of CdSe colloidal quantum dots is studied by pump-probe time-resolved spectroscopy. Infrared pump-probe measurements with ∼6-ps pulses show identical relaxation whether the electron has been placed in the 1Se state by above band-gap photoexcitation or by electrochemical charging. This indicates that the intraband relaxation of the electrons is not affected by the photogenerated holes which have been trapped. However, the surface ligands are found to strongly affect the rate of relaxation in colloid solutions. Faster relaxation (<8ps) is obtained with phosphonic acid and oleic acid ligands. Alkylamines lead to longer relaxation times of ∼10ps and the slowest relaxation is observed for dodecanethiol ligands with relaxation times ∼30ps. It is concluded that, in the absence of holes or when the holes are trapped, the intraband relaxation is dominated by the surface and faster relaxation correlates with larger interfacial polarity. Energy transfer to the ligand vibrations may be sufficiently effective to account for the intraband relaxation rate.