Due to thermal carriers generated by a narrow mid-infrared energy gap, cooling is always necessary to achieve ideal photodetection. In quantum dot (QD), the electron thermal generation should be reduced with quantum confinement in all three dimensions. As a result, there would be a great potential to realize high-operating-temperature (HOT) QD mid-IR photodetectors, though not yet achieved. Taking the advantages of colloidal nanocrystals’ solution processability and precise doping control by surface dipoles, this work demonstrates a HOT mid-infrared photodetector with a QD gradient homojunction. The detector achieves background-limited performance with D^* = 2.7 × 10¹¹ Jones on 4.2 μm at 80 K, above 10¹¹ Jones until 200 K, above 10¹⁰ Jones until 280 K, and 7.6 × 10⁹ Jones on 3.5 μm at 300 K. The external quantum efficiency also achieves more than 77% with responsivity 2.7 A/W at zero bias. The applications such as spectrometers, chemical sensors, and thermal cameras, are also approved, which motivate interest in low-cost, solution-processed and high-performance mid-infrared photodetection beyond epitaxial growth bulk photodetectors.

This perspective describes the advantages of infrared colloidal quantum dots (CQDs) for photodetection beyond silicon and provides a brief review of the development of CQD photodetection. The standard specifications for photodetectors are listed with particular emphasis on the detectivity. High gain improves the responsivity but does not improve the detectivity, while nonradiative losses do not prevent high responsivity but limit the detectivity. Performances of CQD detectors and HgTe CQDs, in particular, are compared with the maximum possible detectivity based on detailed balance from the device temperature and nonradiative losses.