Due to thermal carriers generated by a narrow mid-infrared energy gap, cooling is always necessary to achieve ideal photodetection. In quantum dot (QD), the electron thermal generation should be reduced with quantum confinement in all three dimensions. As a result, there would be a great potential to realize high-operating-temperature (HOT) QD mid-IR photodetectors, though not yet achieved. Taking the advantages of colloidal nanocrystals’ solution processability and precise doping control by surface dipoles, this work demonstrates a HOT mid-infrared photodetector with a QD gradient homojunction. The detector achieves background-limited performance with D^* = 2.7 × 10¹¹ Jones on 4.2 μm at 80 K, above 10¹¹ Jones until 200 K, above 10¹⁰ Jones until 280 K, and 7.6 × 10⁹ Jones on 3.5 μm at 300 K. The external quantum efficiency also achieves more than 77% with responsivity 2.7 A/W at zero bias. The applications such as spectrometers, chemical sensors, and thermal cameras, are also approved, which motivate interest in low-cost, solution-processed and high-performance mid-infrared photodetection beyond epitaxial growth bulk photodetectors.

HgTe colloidal quantum dots are investigated as the active material in photodiodes for extended short-wave infrared up to 2.6 μm. The HgTe colloidal quantum dots photodiodes achieve external quantum efficiencies above 50% and specific detectivities of 1 × 10¹¹ at 2.2 μm at room temperature with a microsecond response time and compete with commercial extended InGaAs photodiodes.