A big challenge in the composites industry is the availability of cheap raw lignocellulosic materials, potential candidates to replace slow growing trees, in order to minimize the production cost. Therefore, a variety of plants were studied and tested worldwide in composites manufacturing. The objective of this study was to investigate the technical feasibility of manufacturing particleboards from seaweed leaves (Possidonia oceanica—PO). The use of such a material may benefit both socioeconomic and environmental development since these leaves settle on seashores and decay. The results showed that an incorporation of up to 10% PO leaves did not significantly affect the mechanical properties of the board. Internal bond strength was more severely affected than the other mechanical properties. The incorporation of PO leaves up to 25% did not significantly improve the dimensional stability of the boards. Markedly, boards made from 50% wood particles and 50% PO leaves showed the best thickness swelling values. It is suggested that higher resin dosage and an alternative resin system, such as isocyanates, may improve the panel properties.

The objective of this paper was to investigate the technical feasibility of manufacturing low density insulation particleboards that were made from two renewable resources, namely hemp fibers (Cannabis sativa) and pine tree bark, which were bonded with a non-toxic methyl cellulose glue, as a binder. Four types of panels were made, which consisted of varying mixtures of tree bark and hemp fibers (tree bark to hemp fibers percentages of 90:10, 80:20, 70:30, and 60:40). An additional set of panels was made, consisting only of bark. The results showed that addition of hemp fibers to furnish improved mechanical properties of boards to reach an acceptable level. The thermal conductivity unfavorably increased as hemp content increased, though all values were still within the acceptable range. Based on cluster analysis, board type 70:30 (with 30% hemp content) produced the highest mechanical properties as well as the optimal thermal conductivity value. It is concluded that low density insulation boards can be successfully produced using these waste raw materials.

Wood, a natural material with versatile industrial applications, faces limitations such as low dimensional stability and decay resistance. To address these issues, there has been significant progress in wood modification research. Oil heat treatment has emerged as an effective method among environmentally friendly wood treatment options. Studies have indicated that treating wood with hot vegetable oils yields superior properties compared to traditional methods involving gaseous atmospheres, which is attributed to the synergistic effect of oils and heat. This comprehensive review investigates the physical, chemical, and mechanical modifications induced by the oil heat treatment of wood, along with its impact on biological durability against biotic agents. The review synthesizes recent research findings, elucidates underlying mechanisms, and discusses the implications for wood material science and engineering.

This research addresses the current need for sustainable solutions in the construction and furniture industries, with a focus on environmentally friendly particleboard. Particleboards were made from a mixture of virgin wood chips and hemp shives, which were then mechanically recycled and used to make new lightweight particleboards. Phenol–formaldehyde resin with 25% w/w phenol replacement by soybean flour (PFS) was used as the binder for the lignocellulosic materials. Laboratory analyses determined the resin properties, and FTIR confirmed the structure of the experimental PFS resin. The thermal properties of all the resins were evaluated using thermogravimetric analysis (TGA). The panels were manufactured using industrial simulation and tested for mechanical and physical properties in accordance with European standards. The FTIR study confirmed good adhesion, and the TGA showed improved thermal stability for the recycled biomass panels compared to virgin biomass panels. The study concludes that lightweight particleboards can be successfully produced from recycled hemp shive-based panels, providing a sustainable alternative to traditional materials in the construction industry.

The aim of this paper was to investigate the physical (thermal transmittance and dimensional stability) and mechanical properties of two types of three layer laminated wood made from fir and meranti; fir in surface layers and meranti in core (FMF) and vice versa (MFM) and to examine its potential application for wood-frame windows. An additional objective was to compare the properties of the laminated wood with those of solid wood, namely meranti and fir. Both types of laminated wood had by far substantial lower bending properties than solid wood. MFM laminated wood performed better than the FMF as far as the physical and mechanical properties are concerned. Water absorption and thickness swelling of MFM laminated wood were substantially lower than those of the FMF type, and all the differences were statistically significant. Longitudinal width swelling, and bending properties of MFM laminated wood were higher than those of FMF but these differences were not statistically significant. The thermal transmittance (rate of the heat transferred) of the FMF window is 13.3% better (less) compared to the MFM window. The main reason for this is believed to be the lower overall density of the FMF window, which also makes it more competitive as a result of the reduced manufacturing cost since fir is less expensive compared tomeranti. It was concluded that wood-frame windows can be successfully made from these types of laminated wood, employing therefore easily renewable materials, with low environmental impact, recyclable and manageable in the medium term.

Wood is a valuable material with incomparable advantages, though it is susceptible to biotic and abiotic factors action that affect it adversely and shorten its service life. In the current study, the surface modification of oak wood is carried out through brief immersion in a solution of acrylic polymer Paraloid B72, in which silica dioxide nanoparticles in the form of nanopowder were dissolved at different contents (1, 2, 3, and 4% w/v of the solution) aiming at the elimination of wood material hygroscopicity, and the protection and improvement of other properties. Specifically, the modified and unmodified wood specimens were characterized in terms of physical characteristics (density, equilibrium moisture content, colour, and surface roughness), hygroscopic properties (swelling and absorption percentage) and accelerated weathering performance using xenon light and cycles of moisturizing and drying. The results revealed the dimensional stability of the samples and a significant increase in the hydrophobicity of the modified wood, as well as a significant increase in the resistance to the ageing/weathering factors of oak wood, which was proportional to the increase in the presence of nanoparticles in the Paraloid B72 solution. The colour of the treated samples slightly changed towards darker shades, more reddish and yellowish (with L* to decrease, while a* and b* to slightly increase), though the treated wood revealed higher colour stability. The surface roughness parameters (Ra, Rq, and Rz) increased significantly, restricting the wide application of the treated wood in indoor or outdoor applications where surface roughness constitutes a critical factor. The findings of the current work contribute not only to the production of longer-lasting wood and timber structures, but also to the conservation of the existing weathered heritage timber structures.