Coal gangue-based geopolymer (CGGP) is one of the hot spots existing in the recycling of coal gangue resources due to its good comprehensive mechanical properties. However, the coal gangue structure is stable and reactivity is poor, so the coal gangue needs to be activated before utilization. In this paper, the microstructure changes of activated coal gangue by different mechanical and thermal activation methods, as well as the mechanical properties and microstructure changes of the CGGP specimens were studied by experimental investigation. The results indicated that mechanical activation and thermal activation were two effective methods to change the reactivity of coal gangue, which consisted of destroying the stable kaolinite structure and improving the activity of coal gangue. Conversely, part of the amorphous structure in coal gangue was destroyed when the activation temperature reached 900 °C, which was not conducive to the further enhancement of coal gangue activity. For the CGGP prepared by thermally activated coal gangue and modified sodium silicate alkali solution, the uniaxial compressive strength of the CGGP specimens decreased with thermal activation temperatures of the raw coal gangue materials at 700 °C, 800 °C, and 900 °C. The main reason for this was the lower amount of the active metakaolin structure in coal gangue at 900 °C, which was not conducive to the geopolymerization process.

Fly ash cement is used to solidify marine clay to prepare marine-clay-based cemented paste backfill (MCCPB) to fill the underground goaf of mines, which not only utilizes solid waste such as fly ash and marine clay, but also controls surface subsidence and protects the environment. To simulate the complex underground mine water environment of the filling body, a dry-wet cycle aquatic environment test under different material ratios and curing ages was designed. The water absorption and unconfined compression strength (UCS) of MCCPB with curing ages of 7 and 28 days under the action of 0, 1, 3, and 7 dry-wet cycles were investigated. The results indicate as the number of dry-wet cycles increases, the surface of MCCPB becomes significantly rougher, and the water content and the solid mass decrease accordingly. Different ratios and curing ages of MCCPB in dry-wet cycles of the UCS tend first to increase, then decrease. Meanwhile, the stress-strain curve of the specimen shows that the trend in the elastic modulus is consistent with that of UCS (first increasing, then decreasing), and that, the minimum UCS value of the specimen still meets the early strength requirements of cemented paste backfill in coal mine geothermal utilization. On the one hand, it proves the feasibility of fly ash cement-solidified marine clay for use as cemented paste backfill in coal mines; on the other hand, it also expands the available range of cemented paste backfill materials in coal mines.

The mining of coal resources is accompanied by a large amount of solid waste such as gangue, which seriously affects the ecological environment. The gangue grouting backfilling technique can achieve the dual goals of gangue disposal and surface deformation control by injecting gangue slurry into the underground. The bearing mechanical characteristics of gangue slurry directly affect the surface deformation control effect of the grouting backfilling technique. In this study, a loading simulation system of grouting backfilling materials was designed, uniaxial confined compression tests were conducted, and the self–bearing mechanism of large particle–sized gangue slurry with different fluidities under instantaneous and creep loading modes was investigated. Additionally, the mechanical characteristics of the compacted body (i.e., the gangue slurry after creep loading) were analyzed. The results indicate that the self–bearing process of gangue slurry can be divided into three stages: the rapid compression and drainage stage, the pore compaction and water bleeding stage, and the particle crushing and elastic–plastic deformation stage. The uniaxial compressive stress–strain curve of a compacted body can be classified into four stages: elastic stage, yield stage, reinforcement stage, and crushing stage, and the strength of the compacted body is affected by the loading time and fluidity of the slurry. When the slurry with a fluidity of 240 mm is subjected to constant pressure for 3 h, the compressive strength of the slurry reaches the maximum value of 4.98 MPa, and 13.1% stress damage occurs when the constant pressure reaches 4 h. This research provides a theoretical basis for the improvement of the proportion and bearing characteristics of gangue grouting materials.