GaN-based high-electron mobility transistors (HEMTs) with AlN/GaN super-lattices (SLs) (4 to 10 periods) as barriers were prepared on (0001) sapphire substrates. An innovative method of calculating the concentration of two-dimensional electron gas (2-DEG) was brought up when AlN/GaN SLs were used as barriers. With this method, the energy band structure of AlN/GaN SLs was analyzed, and it was found that the concentration of 2-DEG is related to the thickness of AlN barrier and the thickness of the period; however, it is independent of the total thickness of the AlN/GaN SLs. In addition, we consider that the sheet carrier concentration in every SL period is equivalent and the 2-DEG concentration measured by Hall effect is the average value in one SL period. The calculation result fitted well with the experimental data. So, we proposed that our method can be conveniently applied to calculate the 2-DEG concentration of HEMT with the AlN/GaN SL barrier.

Dual-wavelength multiple quantum wells (MQWs) have great potential in realizing high quality illumination, monolithic micro light-emitting diode (LED) displays and other related fields. Here, we demonstrate a single chip white light indium gallium nitride (InGaN) LED via the manipulation of the dual-wavelength MQWs. The MQWs contain four pairs of blue light-emitting MQWs and one pair of green light-emitting QW. The fabricated LED chips with nickel/gold (Ni/Au) as the current spreading layer emit white light with the injection current changing from 0.5 mA to 80 mA. The chromaticity coordinates of (0.3152, 0.329) closing to the white light location in the Commission International de I’Eclairage (CIE) 1931 chromaticity diagram are obtained under a 1 mA current injection with a color rendering index (CRI) Ra of 60 and correlated color temperature (CCT) of 6246 K. This strategy provides a promising route to realize high quality white light in a single chip, which will significantly simplify the production process of incumbent white light LEDs and promote the progress of high-quality illumination.

Plasmonic photodetection based on the hot-electron generation in nanostructures is a promising strategy for sub-band detection due to the high conversion efficiencies; however, it is plagued with the high dark current. In this paper, we have demonstrated the plasmonic photodetection with dark current suppression to create a Si-based broadband photodetector with enhanced performance in the short-wavelength infrared (SWIR) region. By hybridizing a 3 nm Au layer with the spherical Au nanoparticles (NPs) formed by rapid thermal annealing (RTA) on Si substrate, a well-behaved ITO/Au/Au NPs/n-Si Schottky photodetector with suppressed dark current and enhanced absorption in the SWIR region is obtained. This optimized detector shows a broad detection beyond 1200 nm and a high responsivity of 22.82 mA/W at 1310 nm at −1 V, as well as a low dark current density on the order of 10⁻⁵ A/cm². Such a Si-based plasmon-enhanced detector with desirable performance in dark current will be a promising strategy for realization of the high SNR detector while keeping fabrication costs low.

The X-ray diffraction pattern is widely used to calculate the periodicity fluctuation of the multiple quantum wells (MQWs). Nonetheless, we find the commonly used formula sometimes couldn't give an exact linear relationship between the full width at half maximum (FWHM) and the satellite peak orders. Here we base on the formula, deduce a more accurate formula to characterize the periodicity fluctuations in InGaN/GaN MQWs. The revised formula has higher linearity correlation degree and the calculated interface roughness coincides well with the X-ray reflectivity (XRR) measurement results.