In this paper, raw natural metakaolin (MK, Serbia) clay was used as a starting material for the synthesis of geopolymers for thermal treatment. Metakaolin was obtained by calcination of kaolin at 750 °C for 1 h while geopolymer samples were calcined at 900 °C, which is the key transition temperature. Metakaolin was activated by a solution of NaOH of various concentrations and sodium silicate. During the controlled heat treatment, the geopolymer samples began to melt slightly and coagulate locally. The high-temperature exposure of geopolymer samples (900 °C) caused a significant reduction in oxygen, and even more sodium, which led to the formation of a complex porous structure. As the concentration of NaOH (6 mol dm⁻³ and 8 mol dm⁻³) increased, new semi-crystalline phases of nepheline and sanidine were formed. Thermal properties were increasingly used to better understand and improve the properties of geopolymers at high temperatures. Temperature changes were monitored by simultaneous use of thermogravimetric analysis (TGA) and differential thermal analysis (DTA). The loss of mass of the investigated samples at 900 °C was in the range of 8–16%. Thermal treatment of geopolymers at 900 °C did not have much effect on the change in compressive strength of investigated samples. The results of thermal treatment of geopolymers at 900 °C showed that this is approximately the temperature at which the structure of the geopolymer turns into a ceramic-like structure. All investigated properties of the geopolymers are closely connected to the precursors and the constituents of the geopolymers.

The aim of this study was determination of physical-chemical and radiological characteristics of kaolin and products of alkali-activated thermally treated kaolin (geopolymer). Also, the objective of presented research was to investigate the possibility of kaolin application as a pigment or as a raw material for obtaining geopolymer materials as a relatively new ones in a building material industry. Physicochemical characterization of one set of samples was conducted using X-ray diffraction (XRD), Fourier transform infra - red (FTIR) and X-ray photoelectron spectroscopy (XPS). Activity concentration of naturally occurring radionuclides in kaolin, metakaolin and geopolymer were determined. The absorbed dose rate (D) and the annual effective dose rate (EDR), calculated in accordance with the UNSCEAR 2000 report, are also presented in this paper. Kaolin was heat-treated on 750oC and specific activity of natural radionuclide in metakaolin increased up to 1.6, while measured specific activities in geopolymer were the lowest.

This paper outlines the production of an inorganic polymer/geopolymer using a metakaolin by an environmental friendly, energy saving, clean technology to conserve natural environment and resources. The influence of alkali activation, i.e. different concentration of NaOH as a component of alkali activator mixture on the process of geopolymerization of metakaolin is investigated. Also, process of aging time of geopolymer is followed by several analytical methods. The structure of metakaolin and metakaolin based geopolymers and their physicochemical properties were studied using X-ray diffraction (XRD), Fourier transformation infrared spectroscopy (FTIR) and after 28days scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) was applied for the surface characterization of the samples. A shift of the Si-O or Si-O-X (X=Al, Si, Na...) bands as the molarity of activator increasing during geopolymerization process was observed by FTIR. Mass spectra of geopolymers were characterized by MALDI TOF mass spectrometer. Structural reorganization of geopolymer samples occurs during the curing/aging in accordance with a geopolymerization mechanism.