The paper describes the influence of the friction stir welding travel speed on the mechanical properties of the butt joints of copper plates. The results of static and fatigue tests of the base material (Cu-ETP R220) and welded specimens produced at various travel speeds were compared, considering a loading applied both parallel and perpendicularly to the rolling direction of the plates. The mechanical properties of the FSW joints were evaluated with respect to parameters of plates’ material in the delivery state and after recrystallisation annealing. The strength parameters of friction stir welding joints were compared with the data on tungsten inert gas welded joints of copper plates available in the literature. The results of microhardness tests and fractographic analysis of tested joints are also presented. Based on the above test results, it was shown that although in the whole range of considered traverse speeds (from 40 to 80 mm/min), comparable properties were obtained for FSW copper joints in terms of their visual and microstructural evaluation, their static and especially fatigue parameters were different, most apparent in the nine-fold greater observed average fatigue life. The fatigue tests turned out to be more sensitive criteria for evaluation of the FSW joints’ qualities.

The work assumed the possibility of the introduction natural fibers as a hybrid reinforcement of bio-polyethylene composites. Coconut fibers, basalt fibers and wood flour were used in different combination as a hybrid merger. Mechanical tests were conducted. An increase in the mechanical properties was shown as an effect of the introduction of the fibers info the polymeric matrix. A synergic influence of hybrid reinforcement was also presented. Experimental results were compared with modeling parameters. The hydrothermal and accelerated thermal ageing effects on the mechanical behavior of composites were presented. Scanning electron microscope images were observed in order to analyze structure of examined composites.

This study investigates the physical and mechanical properties of biodegradable composites based on PLA/PHBV blends modified with different content of nanocrystalline cellulose (NCC) of 5, 10, and 15 wt.%. Density measurements reveal that the density of the composite increases with increasing NCC content. Water absorption tests demonstrate a gradual increase in the composite water content with increasing incubation time, reaching stabilization after approximately 30 days. Mechanical testing was also carried out on both on conditioned samples after the process of hydrolytic degradation and accelerated thermal aging. The conditioned composites show an increase in the stiffness of the materials with increasing content of nanocrystalline cellulose. The ability to deform and the ability to absorb energy when the sample is dynamically loaded decrease. The repeated strength tests, after the process of incubation of samples in water and after the process of accelerated thermal aging, show the degradation of composite materials; however, it is noticed that the introduction of cellulose addition reduces the impact of the applied artificial environment in aging tests. The findings of this study indicate promising applications for these types of materials, characterized by high strength and biodegradability under appropriate conditions. Household items such as various containers or reusable packaging represent potential applications of these composites.

This study examines the relationship between the size of copper particles and the properties of epoxy resin. Epoxy resin is a type of thermosetting resin commonly used as a matrix in polymer matrix composite materials reinforced with glass or carbon fibers. As part of this study, three microscale and two nanoscale composite samples modified with copper oxide particles of varying sizes were produced. This study included mechanical property tests such as static tensile tests, static bending tests, and impact tests. The results of the strength tests were compared to modeling results. Additionally, an accelerated thermal aging process was conducted to determine the impact of external conditions on the behavior of the produced composites. This study concluded with an analysis of thermal conductivity. The test results revealed that the size of the copper particles significantly impacted the tested properties. The composites with copper oxide particles on the nanoscale demonstrated the best results. These composites have promising applications in the automotive and aviation industries due to their strength, resistance to external factors, and increased thermal conductivity, suggesting their potential for producing materials that effectively dissipate heat.

This article’s aim is to analyze physical, mechanical, and fracture properties as well as the thermal investigation of geopolymer composites reinforced with flax, glass fiber, and also the hybrid combination of fibers. Two types of matrices were considered as composites matrices. The first composition was based on fly ash and river sand. The second matrix composition contained fly ash and glass spheres. The content of reinforcement was 1% by mass. Compressive strength and three-point bending fracture tests were performed. The values of fracture toughness and fracture energy were determined. The resonance method was used to verify the dynamic characteristics, such as the dynamic modulus of elasticity and the dynamic Poisson ratio. The results show that single-type fibers in composites based on fly ash and glass spheres did not affect compressive strength. However, introducing hybrid reinforcement increased compressive strength by about 10% compared to the reference specimens. Flax fibers and hybrid reinforcement ensured higher fracture toughness and energy. The results also revealed great potential for glass sphere application to geopolymer materials in terms of fracture mechanics and thermal properties. Despite the lower strength properties in relation to geopolymers based on sand aggregate, applying reinforced fibers into the composite with glass spheres enhanced the compressive strength compared to other materials. Materials modified with glass spheres have a thermal conductivity twice as low as that of materials containing river sand.