An essentially fully acicular alpha-prime martensite within an equiaxed grain structure was produced in an Electron Beam Melting (EBM)-fabricated Ti-6Al-2Sn-4Zr-2Mo (Ti6242) alloy using two different Arcam EBM machines: An A2X system employing tungsten filament thermionic electron emission, and a Q20 system employing LaB6 thermionic electron emission. Post-process Hot Isostatic Pressing (HIP) treatment for 2 h at 850, 950, and 1050 °C resulted in grain refinement and equiaxed grain growth along with alpha-prime martensite decomposition to form an intragranular mixture of acicular martensite and alpha at 850 °C, and acicular alpha phase at 950 and 150 °C, often exhibiting a Widmanstätten (basketweave) structure. The corresponding tensile yield stress and ultimate tensile strength (UTS) associated with the grain growth and acicular alpha evolution decreased from ~1 and ~1.1 GPa, respectively, for the as-fabricated Ti6242 alloy to ~0.8 and 0.9 GPa, respectively, for HIP at 1050 °C. The optimum elongation of ~15–16% occurred for HIP at 850 °C; for both EBM systems. Because of the interactive role played by equiaxed grain growth and the intragrain, acicular alpha microstructures, the hardness varied only by ~7% between 41 and 38 HRC.

This study examines and compares the microstructures, Vickers microindentation hardness, and mechanical properties for additively manufactured (AM) samples built by a variety of AM processes: wire arc AM (WAAM), electron beam powder bed fusion (EB-PBF), laser wire direct energy deposition (LW-DED), electron beam direct energy deposition (EB-DED), laser-powered direct energy deposition (LP-DED), and laser powder bed fusion (L-PBF). These AM process samples were post-processed and heat-treated by stress relief annealing at 1066 °C, HIP at 1163 °C, and solution annealing treatment at 1177 °C. The resulting microstructures and corresponding microindentation hardnesses were examined and compared with the as-built AM process microstructures and hardnesses. Fully heat-treated AM process samples were mechanically tested to obtain tensile properties and were also evaluated and compared. Principal findings in this study were that high-temperature heat treatment >1100 °C of AM process-built samples was dominant and exhibited recrystallized, equiaxed grains containing fcc {111} annealing twins and second phase particles independent of the AM process, in contrast to as-built columnar/dendritic structures. The corresponding yield stress values ranged from 285 MPa to 371 MPa, and elongations ranged from 52% to 70%, respectively. Vickers microindentation hardnesses (HV) over this range of heat-treated samples varied from HV 190 to HV 220, in contrast to the as-built samples, which varied from HV 191 to HV 304.

Inconel 718 alloy fabricated by selective laser melting (SLM) (or laser powder-bed fusion (LPBF)) has been post-process heat-treated by stress-relief anneal at 1065 °C; stress-relief anneal (1065 °C) + solution treatment (at 720 °C) + aging (at 620 °C); hot isostatic pressing (HIP) (at 1120–1200 °C); stress-relief anneal + HIP; and stress-relief anneal + HIP + solution treatment + aging. Microstructure analysis utilizing optical metallography revealed primarily equiaxed grain structures (having average diameters ranging from ~30 to 49 microns) containing annealing twins, and a high concentration of carbide precipitates in all HIP-related treatments in the grain boundaries and intragrain regions. However, no precipitates nucleated on the {111} coherent annealing twin boundaries because of their very low interfacial free energy in contrast to regular grain boundaries. The mechanical properties for the as-fabricated Inconel 718 exhibited a yield stress of 0.64 GPa, UTS of 0.98 GPa, and elongation of 26%. Following stress-relief anneal at 1065 °C, the yield stress dropped to 0.60 GPa, while the elongation increased to 43%. The associated grain structure was an irregular, somewhat elongated, recrystallized structure. This structure was preserved at a stress anneal at 1065 °C + solution treatment + aging, but grain boundary and intragrain precipitation resulted in a doubling of the yield stress to 1.3 GPa and a reduced elongation of 12.6%. The results of HIP-related post-process heat treatments involving temperatures above 1060 °C demonstrated that the yield stress and elongations could be varied from 1.07 to 1.17 GPa and 11.4% to 19%, respectively. Corresponding Rockwell C-scale hardness values also varied from 33 for the as-fabricated Inconel 718 to 53 for simple post-process HIP treatment at 1163 °C.

An unmodified, non-spherical, hydride-dehydride (HDH) Ti-6Al-4V powder having a substantial economic advantage over spherical, atomized Ti-6Al-4V alloy powder was used to fabricate a range of test components and aerospace-related products utilizing laser beam powder-bed fusion processing. The as-built products, utilizing optimized processing parameters, had a Rockwell-C scale (HRC) hardness of 44.6. Following heat treatments which included annealing at 704 °C, HIP at ~926 °C (average), and HIP + anneal, the HRC hardnesses were observed to be 43.9, 40.7, and 40.4, respectively. The corresponding tensile yield stress, UTS, and elongation for these heat treatments averaged 1.19 GPa, 1.22 GPa, 8.7%; 1.03 GPa, 1.08 GPa, 16.7%; 1.04 GPa, 1.09 GPa, 16.1%, respectively. The HIP yield strength and elongation of 1.03 GPa and 16.7% are comparable to the best commercial, wrought Ti-6Al-4V products. The corresponding HIP component microstructures consisted of elongated small grains (~125 microns diameter) containing fine, alpha/beta lamellae.

The fatigue performance of laser powder bed fusion-fabricated Ti-6Al-4V alloy was investigated using four-point bending testing. Specifically, the effects of keyhole and lack-of-fusion porosities along with various surface roughness parameters, were evaluated in the context of pore circularity and size using 2D optical metallography. Surface roughness of S_a = 15 to 7 microns was examined by SEM, and the corresponding fatigue performance was found to vary by 10² cycles to failure. The S–N curves for the various defects were also correlated with process window examination in laser beam power–velocity (P–V) space. Basquin’s stress-life relation was well fitted to the experimental S–N curves for various process parameters except keyhole porosity, indicating reduced importance for LPBF-fabricated Ti-6Al-4V alloy components.