Despite the fact that the electrochemical biosensors based on glucose oxidase represent the golden standard for the management of diabetes, the elaboration of nonenzymatic sensors became extensively studied as an out-of-the-box concept that aims to simplify the existing approach. An important point of view is represented by the low price of the sensing device that has positive effects for both end-users and healthcare systems. The enzyme-free sensors based on low-cost materials such as transition metals have similar analytical properties to the commercial ones while eliminating the issues associated with the presence of the enzyme, such as the stability issues and limited shelf-life. The development of nanoporous nanomaterials for biomedical applications and electrocatalysis was referred to as an alternative to the conventional methods due to their enlarged area, electrical properties, ease of functionalization and not least to their low cost. Herein, we report the development of an electrochemical nonenzymatic sensor for glucose based on 3D copper nanostructures with Ni foams as promotor of the enhanced nanoporous morphology. The sensors were successfully tested in the presence of the designated target, even in the presence of common interference agents found in biological samples.

The paper presents a new approach towards forming Ce-based nanostructures using deep eutectic solvents (DESs) as new green solvents and large-scale media for the chemical and electrochemical synthesis of advanced functional surfaces and nanomaterials. Some experimental results regarding the cathodic electrodeposition of cerium-based conversion coatings onto AA7075 aluminum alloys involving different DES-based formulations are discussed. Electrolytes containing Ce(NO₃)₃·6H₂O dissolved in choline chloride-glycerine and choline chloride-urea (1:2 molar ratio) eutectic mixtures with additions of H₂O₂ have been proposed and investigated. The influence of the operating parameters, including the applied current density, process duration and temperature on the quality of the formed Ce-containing conversion layers was studied. Adherent and uniform Ce-based conversion layers containing 0.3–5 wt.%. Ce have been obtained onto Al alloy substrates. Higher values of the applied current density and longer process durations led to higher Ce content when a choline chloride-urea eutectic mixture was used. Several accelerated corrosion tests were performed to evaluate the corrosion performance, respectively: (i) continuous immersion in 0.5 M NaCl for 720 h with intermediary visual examinations, recording of (ii) potentiodynamic polarization curves and of (iii) impedance spectra at open circuit potential in 0.5 M NaCl, as well as (iv) salt mist test for 240 h. The influence of an additional post-treatment step consisting in the electrochemical deposition of a hydrophobic Ce-based layer involving ethanolic solutions of stearic acid and cerium nitrate is also considered. Different corrosion performances are discussed, taking into account the used DES-based systems and electrodeposition parameters.