The paper presents the test results of basalt fiber impact on a compressive and flexural strength, resistance to abrasion and porosity of Reactive Powder Concrete (RPC). The reasons for testing were interesting mechanical properties of basalt fibers, the significant tensile strength and flexural strength, and in particular the resistance to high temperatures, as well as a relatively small number of RPC tests performed with those fibers and different opinions regarding the impact of those fibers on concrete strength. The composition of the concrete mix was optimized to obtain the highest packing density of particles in the composite, based on the optimum particle size distribution curve acc. to Funk. Admixture of basalt fibers was used in quantity 2, 3, 6, 8 and 10 kg/m³, length 12 mm and diameter 18 µm. A low water-to-binder ratio, i.e., from 0.24, was obtained through application of a polycarboxylate-based superplasticizer. The introduction of up to 10 kg/m³ of basalt fibers to RPC mix was proved to be possible, while keeping the same w/c ratio equal to 0.24, with a slight loss of workability of the concrete mix as the content of fibers increased. It was found that the increase of the fiber content in RPC to 10 kg/m³, despite the w/c ratio was kept the same, caused reduction of the concrete compressive strength by 18.2%, 7.8% and 13.6%, after 2, 7, and 28 days respectively. Whereas, the flexural strength of RPC increased gradually (maximum by 15.9%), along with the fiber quantity increase up to 6 kg/m³, and then it reduced (maximum by 17.7%), as the fiber content in the concrete was further increased. The reduction of RPC compressive strength, along with the increase in basalt fibers content, leads to the increase of the total porosity, as well as the change in pore volume distribution. The reduction of RPC abrasion resistance was demonstrated along with the increase of basalt fibers content, which was explained by the compressive strength reduction of that concrete. A linear relation between the RPC abrasion resistance and the compressive strength involves a high determination coefficient equal to 0.97.

The article describes four-point bending tests of three reinforced concrete beams with identical cross-sections, spans, and high-ductility steel reinforcement systems. Two beams were strengthened in the compressed section with a thin layer of reactive powder concrete (RPC) bonded with evenly spaced stirrups. Their remaining sections, and the third reference beam, were made of ordinary concrete. Measurements of their deflections, strains and axis curvature; ultrasonic tests; and a photogrammetric analysis of the beams are the main results of the study. For one of the beams with the RPC, the load was increased in one stage. For the two remaining beams, the load was applied in four stages, increasing the maximum load from stage to stage in order to allow the analysis of the damage evolution before reaching the bending resistance. The most important effect observed was the stable behaviour of the strengthened beams in the post-critical state, as opposed to the reference beam, which had about two to three times less energy-absorbing capacity in this range. Moreover, thanks to the use of the RPC layer, the process of concrete cover delamination in the compression zone was significantly reduced, the high ductility of the rebars was fully utilized during the formation of plastic hinges, and the bending capacity was increased by approximately 12%.

Reactive powder concrete (RPC), typically with higher compressive strength, is particularly attractive to structural engineers to apply them in infrastructures for enhancing their resistance under severe environments and loads. The main objective of the initial study presented in the paper was to investigate the behavior of two types of these new cementitious materials differing in the nature of microfibers. The RPC mixes were reinforced with steel and then with basalt microfibers. To evaluate the structural performance of developed unconventional materials, properties were investigated experimentally and compared with the control normal concrete mix. Mechanical tests indicated that dispersing fine fibers for making RPC, a mean compressive strength of 198.3 MPa and flexural strength 52.6 MPa or 23.2 MPa, respectively, were developed after 28 days of standard curing at ambient temperatures. In composite structures consisting of steel girders and a concrete slab, it is necessary to prevent the relative slip at the steel and concrete interface using shear connectors. The very high RPC strength enabled a material saving, weight-reduced application of precast construction, and particularly effective joint to steel beams. The investigation of such shear connection efficiency, in the case of the higher strength concrete deck, using standard push-out test specimens was executed. Finite element numerical models were developed. The outputs of the studies are presented in the paper.

This paper presents test results of the impact of chemical admixtures used in the underwater concrete technology, i.e. a superplasticizer (SP), an anti-wash admixture (AWA) and SiO2 nano- particles (NP) on the cement hydration process, rheological properties and the setting time. The impact of admixtures was tested in combination and separately, with the use of microcalimetry, X-ray diffraction (XRD) and rheology. It was demonstrated that AWA and SP admixtures caused a delay of the hydration process, while the impact of SP was much greater. The above statement was also confirmed by results of rheological tests. Combined application of AWA, SP and NP causes even a larger delay of the hydration process and the increase of paste rheological parameters, with the impact of the superplasticizer particularly visible.

Reducing CO₂ emissions from cement production is currently one of the major challenges faced by the cement industry. One approach to lowering these emissions is to reduce the clinker factor by incorporating alternative mineral additives into cement. Consequently, there is a growing interest in the use of copper slags (CSs) as supplementary cementitious materials. Therefore, this study investigates the properties of cements containing substantial amounts of copper slag (up to 60%) and, for comparison, the same proportions of granulated blast furnace slag. The inclusion of substantial amounts of CS results both from the lack of studies in this area and from the potential benefits associated with the utilization of larger quantities of copper slag. The chemical, phase, and particle size composition of CS and granulated blast furnace slag added to CEM I 42.5 cement from the Odra cement plant in amounts of 20%, 40%, and 60% by weight were compared. The pozzolanic activity index of the copper slag and the hydraulic activity index of the blast furnace slag were determined. The high pozzolanic activity of the CS was attributed to its high degree of vitrification (nearly 100%). In contrast, the lower hydraulic activity of the blast furnace slag was explained by its lower glass phase content (about 90% by mass). A gradual decrease in the total heat of hydration released within the first two days was observed with increasing slag content in the cement, slightly more pronounced for copper slags. However, at later stages (2–28 days), XRD analysis indicated higher hydration activity in cements containing copper slag, resulting from its strong pozzolanic reactivity. Cements with copper slag also showed slightly lower water demand compared to those with blast furnace slag. An increase in setting time was observed with higher slag content, more noticeable for blast furnace slag. The type and amount of slag in cement reduce both yield stress and plastic viscosity. Greater reductions were observed at higher slag content. Moreover, copper slag caused greater paste fluidity, attributed to the lower amount of fine particles fraction. The addition of slag decreased flexural and compressive strength in the early period (up to 7 days), this reduction being proportional to slag content. After 90 days, mortars containing 20% and 40% copper slag achieved strength values exceeding that of the reference mortar by 4%. In contrast, at a 60% CS content, a 5% decrease was observed, while for cement with 60% BFS the decrease was 11%. This indicates that a lower copper slag content in the cement (40%) is more favorable in terms of strength.