Biodiesel is a potential alternative for fossil fuel. However, its large-scale application is held up by the disadvantage of a homogenous process, the scarce availability of raw materials and the production cost, which is higher than for fossil diesel. In this work, biodiesel production was carried out using both refined and used cooking oils. The process was investigated in a batch reactor, in the presence of CaO as a heterogeneous catalyst prepared by the calcination of the natural Waste Grooved Razor Shell (GRS). Characterizations by X-Ray Diffraction (XRD) and Thermal Gravimetric (TG)/Differential Thermal Analysis (DTA) showed that the as-received GRS consists of aragonite, (i.e., CaCO₃) as the main component and of water and organic matter in a lower amount. After calcination at 900 °C, CaO was formed as the only crystalline phase. The effects of several experimental parameters in the transesterification reactions were studied, and their impact on the produced biodiesel properties was investigated. The studied variables were the methanol/oil molar ratio, the catalyst weight percentage (with respect to the oil mass), the calcination temperature of the parent GRS and the recycling and regeneration of the catalyst. The physico-chemical and fuel properties, i.e., viscosity, density and acid value of used oils and of the produced biodiesel, were determined by conventional methods (American Society for Testing and Materials (ASTM) methods) and compared with the European standards of biodiesel. The optimal identified conditions were the following: the use of a 15:1 methanol/oil molar ratio and 5 wt% of CaO with respect to the oil mass. After 3 h of reaction at 65 °C, the biodiesel yield was equal to 94% and 99% starting from waste and refined oils, respectively.

Microbial fuel cells (MFCs) are an environmentally friendly technology that can recover electricity directly from several wastes at ambient temperatures. This work explores the use of mineral oil refinery wastewater as feedstock in single-chamber air-cathode MFC devices. A polymer inclusion membrane based on the ionic liquid methyltrioctylammonium chloride, [MTOA⁺][Cl⁻], at a concentration of 70% w/w, was used as separator, showing a good efficiency in power production and chemical oxygen demand (COD) removal. The power and the chemical oxygen demand removal reached values of 45 mW/m³ and over 80%, respectively. The evolution of other parameters of the wastewater including nitrites, phosphates and sulphates were also studied. Kjeldahl nitrogen and sulphates were significantly reduced during MFC operation. The results show that mineral oil refinery wastewater can be used as feedstock in air breathing cathode-microbial fuel cells based on polymer ionic liquid inclusion membranes. This configuration could represent a good alternative for wastewater depuration while producing energy during the process.

Microbial fuel cells (MFCs) provide new opportunities for the sustainable production of energy, converting organic matter into electricity through microorganisms. Moreover, MFCs play an important role in remediation of environmental pollutants from wastewater with power generation. This work focuses on the evaluation of ferroelectric perovskite materials as a new class of non-precious photocatalysts for MFC cathode construction. Nanoparticles of BaTiO₃ (BT) were prepared and tested in a microbial fuel cell (MFC) as photocathode catalytic components. The catalyst phases were synthesized, identified and characterized by XRD, SEM, UV–Vis absorption spectroscopy, P-E hysteresis and dielectric measurements. The maximum absorption of BT nanoparticles was recorded at 285 nm and the energy gap (Eg) was estimated to be 3.77 eV. Photocatalytic performance of cathodes coated with BaTiO₃ was measured in a dark environment and then in the presence of a UV–visible (UV–Vis) light source, using a mixture of dairy industry and domestic wastewater as a feedstock for the MFCs. The performance of the BT cathodic component is strongly dependent on the presence of UV–Vis irradiation. The BT-based cathode functioning under UV–visible light improves the maximum power densities and the open circuit voltage (OCV) of the MFC system. The values increased from 64 mW m⁻² to 498 mW m⁻² and from 280 mV to 387 mV, respectively, showing that the presence of light effectively improved the photocatalytic activity of this ceramic. Furthermore, the MFCs operating under optimal conditions were able to reduce the chemical oxygen demand load in wastewater by 90% (initial COD = 2500 mg L⁻¹).

The environmental pollution caused by organic molecules as Tetracyclines and Oxytetracyclines presents a foremost concern, as high levels of these antibiotics when released into the ecosystem are accumulated and are producing overall contamination. Consequently, the need for selective, sensitive, fast, easy to handle, and low-cost early monitoring detection systems is growing. Electrochemical sensors based on modified carbon electrodes involve relevant materials for antibiotics’ detection, which allows the early controlling of the spread of these antibiotics into the environment, thus, safeguarding human health against possible contamination. The present review paper has aimed to illustrate examples of newly developed electrochemical bio(chemo)sensors with their real application fields for the sensitive detection of Tetracycline as well as Oxytetracycline in various matrices. Future forecast for the utilisation of these sensors is also discussed.

The present work is the first investigation of the electrocatalytic performances of ZrP₂O₇ as a cathode in a single-chamber Microbial Fuel Cell (MFC) for the conversion of chemical energy from wastewater to bioelectricity. This catalyst was prepared by a coprecipitation method, then characterized by X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), ultraviolet–visible–near-infrared spectrophotometry (UV–Vis–NIR), and cyclic voltammetry analyses. The acid–basic characteristics of the surface were probed by using 2-butanol decomposition. The conversion of 2-butanol occurs essentially through the dehydrating reaction, indicating the predominantly acidic character of the solid. The electrochemical test shows that the studied cathode material is electroactive. In addition, the ZrP₂O₇ in the MFC configuration exhibited high performance in terms of bioelectricity generation, giving a maximum output power density of around 449 mW m⁻²; moreover, it was active for wastewater treatment, reducing the chemical oxygen demand (COD) charge to 50% after three days of reaction.