To solve the problem of poor weldability between TiAl-based and Ti₂AlNb-based alloys, spark plasma diffusion bonding was employed to join a TiAl alloy and a Ti₂AlNb alloy with a pure Ti foil as interlayer at 950 °C/10 KN/60 min. After welding, slow cooling was carried out at a rate of 5 °C/min, followed by homogenization at 800 °C for 24 h. The microstructural evolution and elemental migration of the joint were analyzed via a scanning electron microscope equipped with an energy dispersive spectrometer, while the mechanical properties of the joint were assessed via microhardness and tensile tests. The results show that the spark plasma diffusion bonding formed a joint of TiAl/Ti/Ti₂AlNb without microcracks or microvoids, while also effectively protecting the base metal. Before heat treatment, the maximum hardness value (401 HV) appeared at the Ti₂AlNb/Ti interface, while the minimum hardness value (281 HV) occurred in the TiAl base metal. The tensile strength of the heat-treated joint at room temperature was measured to be up to 454 MPa, with a brittle fracture occurring in the interlayer. The tensile strength of the joint at 650 °C was measured to be up to 538 MPa, with intergranular cracks occurring in the TiAl base metal.

In this paper, spark plasma diffusion bonding technology was employed to join TiAl and Ti₂AlNb with high temperature titanium alloy interlayer at 950 °C/10kN/60 min, then following furnace cooling at cooling rate up to 100 °C/min. After welding, the joint was aging heat-treated at 800 °C for 24 h. The microstructure and the elements diffusion of the TiAl/Ti₂AlNb joint was analyzed by field emission scanning electron microscopy (FESEM) with EDS. Moreover, the tensile properties of the joint were tested at room temperature, 650 °C, and 750 °C. The results show that the spark plasma diffusion bonding formed a high quality TiAl/Ti₂AlNb joint without microcracks or microvoids, while also effectively protecting the base metal. Significant differences in the microstructure of the joint appeared from TiAl side to Ti₂AlNb side: TiAl BM (Base Metal) → DP(Duplex) and NG (Near-Gamma) → α₂-phase matrix with needle-like α-phase → bulk α₂-phase → needle-like α-phase → metastable β-phase → Ti₂AlNb BM. After heat treatment at 800 °C for 24 h, the microstructure of the TiAl side and the interlayer region did not change, but the density and size of the needle-like α-phase in region 3 increased slightly. The microstructure of Ti₂AlNb near the weld changed obviously, and a large number of fine O phases are precipitated from the metastable β phase matrix after heat treatment. Except for the Ti₂AlN near-interface region, the effect of heat treatment on the microstructure of the joint is not significant. The microhardness of the joint is in the shape of a mountain peak. The maximum microhardness at the interface is above 500 HV, and it is significantly reduced to 400 HV after heat treatment. The fracture of the joint occurred at the interface at room temperature, 650 °C, and 750 °C. with the tensile strength 450 MPa, 540 MPa, and 471 Mpa, respectively, and mainly showing brittle fracture.