The impregnation of low-molecular-weight monomers prior to polymerize them inside the wood may be an efficient way to improve some important wood properties. This work aimed to determine some technological properties of wood-based composites (WPC) produced by in situ polymerization, using a pine wood (Pinus elliottii Engelm.) impregnated with methyl methacrylate (MMA). For that, samples taken from both juvenile (JV) and mature (MT) pine woods were treated with MMA. Physical, mechanical, chemical, thermal and morphological features were evaluated. MMA-treated woods from both juvenile and mature woods presented superior physical, mechanical (expect brittleness) and thermal properties when compared to pristine ones. The infrared spectra and morphological analysis by scanning electron microscopy (SEM) confirmed the presence of the monomer inside the pine wood. The juvenile wood presented higher treatability than the mature wood, due to its higher content of intra- and inter-cellular spaces.

This study aimed to analyze chemical changes by Fourier Transform Infrared Spectroscopy of Eucalyptus dunnii and Pinus elliottii treated woods subjected to an accelerated decay test with the white rot fungus Ganoderma applanatum. The wood test specimens (2,5x2,5x0,9 cm) were impregnated with preservative solutions of chromated copper borate and synthetic pyrethroids and carbamates with 6% concentration by a vaccum-pressure process. After a decay test of 16 weeks, the chemical changes of the treated and untreated wood samples were evaluated by Fourier Transform Infrared Spectroscopy. It was observed that the rot fungus attack caused a variation in the intensity and a displacement of spectrum peaks, indicating a change to the woods’ chemical composition after fungal exposure. The lignin / carbohydrate ratio indicated that the fungus had no preference for a specific cell wall component, pointing to a simultaneous deterioration of cellulose, hemicellulose and lignin in the treated and untreated woods. Finally, the Fourier Transform Infrared Spectroscopy technique, together with the lignin / carbohydrate ratio analysis, proved efficient in the study of the variation of the wood chemical modifications deteriorated by rot fungi.

O Pinus elliottii Engelm. possui uma vasta possibilidade de aplicações, porém, apresenta características indesejáveis às quais podem ser atenuadas com a adoção dos tratamentos de termorretificação e a furfurilação. Assim, este trabalho analisou a influência que os tratamentos de furfurilição e termorretificação exerceram em propriedades tecnológicas da madeira de Pinus elliottii. Para tanto, confeccionaram-se corpos de prova com dimensões de 15 x 15 x 250 mm (tangencial, radial e longitudinal), distribuídos igualmente em 5 tratamentos: controle, furfurilação com carga de 25% de álcool furfurílico (T F25%) e termorretificação em diferentes temperaturas (T 180°C, T 200°C e T 220°C). Avaliaram-se a variação da massa (ΔM) segundo adaptação da norma ASTM D 2017 (2005), à massa específica aparente ao teor de umidade de 12% (ρ12%), os módulos de elasticidade (MOE) e ruptura (MOR) obtidos pelo ensaio de flexão estática conforme a norma ASTM D 143 (2014), e a variação colorimétrica da madeira em conformidade com as recomendações do sistema CIE-L*a*b*. Verificou-se que o tratamento com furfurol provocou: aumentos significativos na massa, ρ12%, MOR, e causou o escurecimento da madeira, não afetando significativamente o MOE, em 5% de probabilidade de erro. Os tratamentos de termorretificação afetaram significativamente a perda de massa, contudo a maior diferença foi observada no tratamento T 220°C, o qual acarretou redução significativa no MOR em relação ao grupo controle, destacando-se que tal tratamento deixou a madeira com coloração semelhante aquela adquirida pela madeira tratada com furfurol. Conclui-se que ambos os tratamentos causaram o escurecimento da madeira de Pinus elliottii agregando assim valor estético, sendo que o tratamento à base de furfurol, com carga de 25%, ocasionou melhora nas propriedades tecnológicas da madeira. Apesar dos tratamentos de termorretificação terem aumentado o MOE, geraram perda de massa significativa, principalmente nos tratamentos mais agressivos, comprometendo assim possíveis usos da madeira com finalidade estrutural.

A wood-based polymer composite was manufactured and characterized using in situ polymerization of styrene into juvenile and mature pine wood. Treatment parameters and properties were evaluated by using infrared spectroscopy, thermogravimetry and mechanical testing. Specimens treated by in-situ polymerization of styrene showed increased thermal stability as well as improved mechanical properties.

RESUMO O interesse pela síntese de nanopartículas utilizando extratos vegetais vem crescendo nas últimas décadas, devido a não geração de resíduos de químicos tóxicos e condições mais brandas de síntese. O Brasil é um dos líderes em florestas plantadas, principalmente do gênero Eucalyptus, em razão disso o objetivo deste trabalho foi sintetizar nanopartículas de óxido de zinco utilizando extrato etanólico das folhas de Eucalyptus dunnii. As folhas foram secas e moídas para obtenção de pó, 10 g deste foram adicionadas em 100 mL de álcool etílico, a solução foi mantida em banho-maria a 80 ºC por 75 min, a solução foi filtrada para obtenção do extrato. Para a síntese utilizou-se 20 mL de extrato e 1,57 g de acetato de zinco, a solução foi mantida a 80 ºC sob agitação magnética vigorosa por 20 min, transcorrido o tempo foi realizado tratamento térmico em mufla a 500 ºC por 2h. As nanopartículas obtidas apresentaram característica cristalina e diâmetro médio de 32,24 nm. O espectro FTIR do extrato apresentou diversos picos relacionados a compostos redutores capazes de realizar a síntese, enquanto o espectro das nanopartículas demonstrou que mesmo após a calcinação, ainda se detecta a presença de compostos orgânicos que podem ser responsáveis pela estabilização das mesmas. Sendo assim, o extrato etanólico de E. dunnii possui capacidade redutora para realizar a síntese de nanopartículas cristalinas de óxido de zinco.

O conhecimento sobre as propriedades tecnológicas da madeira possibilita a obtenção de ferramentas que auxiliem na utilização adequada desse material. Portanto, o objetivo desse estudo foi realizar a caracterização tecnológica da madeira de Eucalyptus benthamii para potenciais utilizações. Para isso, utilizaram-se seis indivíduos arbóreos de um plantio florestal implantado na cidade de Guatambu, Santa Catarina. Para a caracterização física da madeira, foram retirados discos em três posições distintas do fuste de cada árvore, determinando a massa específica básica e a retratibilidade. Os corpos de prova para os ensaios mecânicos de compressão paralela às fibras, flexão dinâmica, flexão estática e dureza Janka foram obtidos de discos retirados das toras.