The present research work had the goal of assessing the use of ultrasound for determining the physical-mechanical properties of clear wood in Eucalyptus camaldulensis from a 5-year-old forest stand located in the municipality of Sinop, Mato Grosso State, Brazil. The selection of trees was carried out according to the diameter at breast height (DBH) and height (H). Forty trees were harvested and a 2 m long log was obtained from each tree for the assessment of physical-mechanical properties. In physical properties, the specific gravity, shrinkage (radial, tangential and volumetric) and anisotropic factor were determined. The dynamic modulus of elasticity (MOE) was estimated by ultrasound applied in the longitudinal direction of the samples. The highest correlation with the mechanical test results was found for dynamic MOE, with R² values in the range of 0.30–0.75. Wood density was highly positively correlated with the dynamic MOE of the wood. The use of ultrasound as a non-destructive method was feasible to determine the selected physical-mechanical properties of Eucalyptus camaldulensis wood as a function of propagation speed and the MOE dynamic in most of the assays.

The impregnation of low-molecular-weight monomers prior to polymerize them inside the wood may be an efficient way to improve some important wood properties. This work aimed to determine some technological properties of wood-based composites (WPC) produced by in situ polymerization, using a pine wood (Pinus elliottii Engelm.) impregnated with methyl methacrylate (MMA). For that, samples taken from both juvenile (JV) and mature (MT) pine woods were treated with MMA. Physical, mechanical, chemical, thermal and morphological features were evaluated. MMA-treated woods from both juvenile and mature woods presented superior physical, mechanical (expect brittleness) and thermal properties when compared to pristine ones. The infrared spectra and morphological analysis by scanning electron microscopy (SEM) confirmed the presence of the monomer inside the pine wood. The juvenile wood presented higher treatability than the mature wood, due to its higher content of intra- and inter-cellular spaces.

Pine seed shells and yerba mate are common wastes leftover from the food and beverage industry. This study presents the development of rigid polyurethane foams (RPUFs) filled with pine seed shells and yerba mate at 5, 10 and 15 wt%. The fillers were characterized for chemical properties using bench chemistry analyses, and the RPUFs were investigated in terms of chemical, morphological, mechanical, thermal and colorimetric characteristics. The main results indicated that yerba mate showed good compatibility with the polyurethane system, probably because its available hydroxyl groups reacted with isocyanate groups to form urethane bonds, producing increases in mechanical and thermal properties. However, pine seed shell did not appear to be compatible. Anisotropy increased slightly, as there was an increase in the percentage of reinforcement. The mechanical properties of the yerba mate reinforced foams proved stable, while there was a loss of overall up to ~50% for all mechanical properties in those reinforced with pine seed shell. Thermal properties were improved up to ~40% for the yerba mate reinforced foams, while those reinforced with pine nuts were stable. It was possible to observe a decrease in the glass transition temperature (T_g) of ~−5 °C for the yerba mate reinforced foams and ~−14 °C for the pine seed shell reinforced ones.

Developing a new type of polyurethane is essential because conventional options often exhibit shortcomings in terms of environmental sustainability, cost-effectiveness, and performance in specialized applications. A novel polyurethane adhesive derived from a simple mixture of castor oil (CO) and crude glycerin (CG) holds promise as it reduces reliance on fossil fuels and harnesses renewable resources, making it environmentally friendly. Simple CO/CG mixtures, adjusted at three different weight fractions, were used as bio-based polyester polyols to produce polyurethane adhesive for wood bonding. The resulting products are yellowish liquids with moderate-to-high viscosity, measuring 19,800–21,000 cP at 25 °C. The chemical structure of the polyester polyols was characterized using infrared spectroscopy (FTIR), thermogravimetry (TG), and differential scanning calorimetry (DSC). These polyols reacted with polymeric 4,4-methylene diphenyl diisocyanate (p-MDI) at a consistent isocyanate index of 1.3, resulting in the formation of polyurethane adhesives. Crucially, all final adhesives met the adhesive strength requirements specified by ASTM D-5751 standards, underscoring their suitability for wood bonding applications. The addition of CG enhanced the surface and volumetric hydrophobicity of the cured adhesives, resulting in adhesive properties that are not only stronger but also more weather-resistant. Although the thermal stability of the adhesives decreased with the inclusion of CG, FTIR analysis confirmed proper polyurethane polymer formation. The adhesive adjusted for a 2:1 CO:CG weight ratio promoted wood–wood bonding with the highest shear strength, likely due to a higher formation of urethane linkages between hydroxyl groups from the blend of polyols and isocyanate groups from the p-MDI.

This study aims to compare the resistance against subterranean termites of wood–polymer composites produced by in situ polymerization. The biological tests were carried out by choice and no-choice feeding tests. Poly (furfuryl alcohol), poly(styrene) and poly (methyl methacrylate) were studied here. They were impregnated into a Brazilian fast-growing pine wood using a vacuum:pressure method and then cured under simple heating. These treatments were evaluated using chemical (by infrared spectroscopy) and morphological (by scanning electron microscopy) analyses. The termite attack was evaluated by mass loss determination and photography. In general, all the treatments were effective in protecting the fast-growing pine wood. Results obtained by no-choice tests indicated that the treatment solution with 75% of furfuryl alcohol was less effective than the others, which indicates that both choice and no-choice tests may be important in a comprehensive study on the termites resistance of solid woods.