Materials possessing long-term antibacterial behavior and high cytotoxicity are of extreme interest in several applications, from biomedical devices to food packaging. Furthermore, for the safeguard of the human health and the environment, it is also stringent keeping in mind the need to gather good functional performances with the development of ecofriendly materials and processes. In this study, we propose a green fabrication method for the synthesis of silver nanoparticles supported on oxidized nanocellulose (ONCs), acting as both template and reducing agent. The complete structural and morphological characterization shows that well-dispersed and crystalline Ag nanoparticles of about 10–20 nm were obtained in the cellulose matrix. The antibacterial properties of Ag-nanocomposites (Ag–ONCs) were evaluated through specific Agar diffusion tests against E. coli bacteria, and the results clearly demonstrate that Ag–ONCs possess high long-lasting antibacterial behavior, retained up to 85% growth bacteria inhibition, even after 30 days of incubation. Finally, cell viability assays reveal that Ag-ONCs show a significant cytotoxicity in mouse embryonic fibroblasts.

The fracture surfaces of a 10.5 wt.% Cr martensitic stainless steel broken in Charpy tests have been investigated through X-ray photoelectron spectroscopy (XPS). The specimens have been examined in two different conditions: as-quenched and heat treated for 10 h at 700 °C. The trends of Fe/Cr ratio vs. test temperature are similar to the sigmoidal curves of absorbed energy and, after both ductile and quasi-cleavage brittle fractures, such ratio is always significantly lower than the nominal value of the steel chemical composition. Cr segregation does not occur on a macroscopic scale but takes place in microscopic zones which represent weaker spots in the steel matrix and a preferred path for moving cracks. Small area (diameter 300 µm) XPS measurements evidenced a higher density of such microscopic zones in the inner part of probes; this is explained by the different diffusion length of Cr atoms in the external and inner parts during quenching from austenitic field which has been calculated through FEM simulations. No significant differences of Cr concentration were observed in fracture surfaces of probes with and without heat treatment. The results highlight how Cr segregation plays a role not only in the intergranular mode of fracture but also in the quasi-cleavage and ductile ones.

Surfaces of commercial molybdenum (Mo) plates have been textured by fs-laser treatments with the aim to form low-cost and efficient solar absorbers and substrates for thermionic cathodes in Concentrated Solar Power conversion devices. Morphological (SEM and AFM), optical (spectrophotometry), and structural (Raman spectroscopy) properties of the samples treated at different laser fluences (from 1.8 to 14 J/cm²) have been characterized after the laser treatments and also following long thermal annealing for simulating the operating conditions of thermionic converters. A significant improvement of the solar absorptance and selectivity, with a maximum value of about four times higher than the pristine sample at a temperature of 800 K, has been detected for sample surfaces treated at intermediate fluences. The effects observed have been related to the light trapping capability of the laser-induced nanotexturing, whereas a low selectivity, together with a high absorptance, could be revealed when the highest laser fluence was employed due to a significant presence of oxide species. The ageing process confirms the performance improvement shown when treated samples are used as solar absorbers, even though, due to chemical modification occurring at the surface, a decrease of the solar absorptance takes place. Interestingly, the sample showing the highest quantity of oxides preserves more efficiently the laser texturing. The observation of this behaviour allows to extend the applicability of the laser treatments since, by further nanostructuring of the Mo oxides, it could be beneficial also for sensing applications.