Spontaneous voltage drop between EDLC electrodes, when it is kept under the open-circuit condition, is commonly called ‘self-discharge’ and is interpreted as a result of energy loss by the device. Three mechanisms of self-discharge were proposed: due to a leakage-current, faradaic reactions and charge redistribution. According to the law of energy preservation, if the voltage drop is associated with the energy loss, the energy would more likely be exchanged with the environment. While heat generation was measured during EDLC charging and discharging, the corresponding effect during storage under open-circuit conditions has not been reported. This may support the conclusion that voltage changes during ‘self-discharge’ are not related to a considerable energy loss. Moreover, it has been shown that a two-stage charging process, i.e. first galvanostatic charging followed by a potentiostatic charge redistribution, resulted in considerably slower potential changes when the device was switched to the open circuit. All discussed models were based on the assumption that the energy accumulated by EDLCs is proportional to the voltage in the second power, with capacitance (C/2) as the proportionality constant. However, it has been shown that during EDLC charging or discharging through a resistance R, equations valid for ‘dielectric’ and electrolytic capacitors, do not hold in the case of EDLCs. Consequently, the assumption that the energetic state of the EDLC is proportional at any time to the voltage in the second power may not be valid due to considerable variability of the ‘constant’ C. Therefore, voltage changes may not reflect the energetic state of the device.

This study reveals a simple approach to recycle wasted coffee grounds into highly valuable carbon material with superior electrochemical performance. Activated carbon prepared from wasted coffee grounds has been formed via hydrothermal acidic hydrolysis followed by a KOH chemical activation at 800 ${}^{\circ }\mathrm{C}$. To understand the electrochemical properties of the sample, a set of characterization tools has been utilized: N₂ and CO₂ adsorption–desorption isotherms, thermal gravimetric analysis, Fourier transform infrared spectroscopy, Raman spectroscopy and scanning electron microscopy. The specific surface area obtained from a Brunner–Emmett–Teller (BET) analysis reached $2906\pm 19$$\mathrm{m}$${}^2$${\mathrm{g}}^{-1}$. Prepared sample (designated as ACG-800KOH) was tested as electrode material in an electric double layer capacitor (EDLC) device with ionic liquid PYR13-TFSI as an electrolyte. The EDLC test was conducted at temperatures ranging from 20 to 120 ${}^{\circ }\mathrm{C}$. The specific material capacitance reached 178 $\mathrm{F}$${\mathrm{g}}^{-1}$ measured at 20 ${}^{\circ }\mathrm{C}$ and 50 A ${\mathrm{g}}^{-1}$ and was in the range 182 to 285 $\mathrm{F}$${\mathrm{g}}^{-1}$ at the 20 to 120 ${}^{\circ }\mathrm{C}$ temperature range.

The renewable energy technologies require electrocatalysts for reactions, such as the oxygen and/or hydrogen evolution reaction (OER/HER). They are complex electrochemical reactions that take place through the direct transfer of electrons. However, mostly they have high over-potentials and slow kinetics, that is why they require electrocatalysts to lower the over-potential of the reactions and enhance the reaction rate. The commercially used catalysts (e.g., ruthenium nanoparticles—Ru, iridium nanoparticles—Ir, and their oxides: RuO₂, IrO₂, platinum—Pt) contain metals that have poor stability, and are not economically worthwhile for widespread application. Here, we propose the spinel structure of nickel-cobalt oxide (NiCo₂O₄) fabricated to serve as electrocatalyst for OER. These structures were obtained by a facile two-step method: (1) One-pot solvothermal reaction and subsequently (2) pyrolysis or carbonization, respectively. This material exhibits novel rod-like morphology formed by tiny spheres. The presence of transition metal particles such as Co and Ni due to their conductivity and electron configurations provides a great number of active sites, which brings superior electrochemical performance in oxygen evolution and good stability in long-term tests. Therefore, it is believed that we propose interesting low-cost material that can act as a super stable catalyst in OER.