We present an investigation consisting of single walled carbon nanotubes (SWCNTs) based cryogenic temperature sensors, capable of measuring temperatures in the range of 2–77 K. Carbon nanotubes (CNTs) due to their extremely small size, superior thermal and electrical properties have suggested that it is possible to create devices that will meet necessary requirements for miniaturization and better performance, by comparison to temperature sensors currently available on the market. Starting from SWCNTs, as starting material, a resistive structure was designed. Employing dropcast method, the carbon nanotubes were deposited over pairs of gold electrodes and in between the structure electrodes from a solution. The procedure was followed by an alignment process between the electrodes using a dielectrophoretic method. Two sensor structures were tested in cryogenic field down to 2 K, and the resistance was measured using a standard four-point method. The measurement results suggest that, at temperatures below 20 K, the temperature coefficient of resistance average for sensor 1 is 1.473%/K and for sensor 2 is 0.365%/K. From the experimental data, it can be concluded that the dependence of electrical resistance versus temperature can be approximated by an exponential equation and, correspondingly, a set of coefficients are calculated. It is further concluded that the proposed approach described here offers several advantages, which can be employed in the fabrication of a microsensors for cryogenic applications.

The laser excitation of magnetization dynamics without applying external fields is a topic of high interest for its potential applications (e.g., magnetic memories, oscillators, and THz emitters). We explore the use of an ultrashort infrared laser pulse for triggering transient changes in a magnetic vortex, probing the induced dynamics by time-resolved magnetic helicoidal dichroism (MHD) in resonant extreme ultraviolet scattering. MHD describes the optical response of a magnetic sample upon sign reversal of either the light orbital angular momentum or the magnetization and was demonstrated to be sensitive to the sample spin texture. Here, we show that, in addition to the well-known ultrafast demagnetization and remagnetization laser-induced processes, the analysis of the MHD signal, supported by micromagnetic simulations, provides direct evidence of important transient reorganizations of the spin texture. In particular, we find that an ultrafast laser pulse of sufficient intensity can induce a surface transient magnetic texture where the vortex curling direction is reversed with respect to the bulk. This result provides insight into the preparation of metastable complex spin states in magnetic films by optical methods without applying an external field, which is of relevance for novel applications in data storage and manipulation.

Epitaxial La_0.7Sr_0.3MnO₃ films with different thicknesses (9–90 nm) were deposited on SrTiO₃ (0 0 1) substrates by pulsed laser deposition. The films have been investigated with respect to morpho-structural, magnetic, and magneto-transport properties, which have been proven to be thickness dependent. Magnetic contributions with different switching mechanisms were evidenced, depending on the perovskite film thickness. The Curie temperature increases with the film thickness. In addition, colossal magnetoresistance effects of up to 29% above room temperature were evidenced and discussed in respect to the magnetic behavior and film thickness.

The manipulation of magnetic anisotropy represents the fundamental prerequisite for the application of magnetic materials. Here we present the vectorial magnetic properties of nanostructured systems and thin films of Fe and FeCo prepared on linearly trenched Mo templates with thermally controlled periodicity. The magnetic properties of the nanosystems are engineered by tuning the shape, size, thickness, and composition parameters of the thin films. Thus, we control coercivity, magnetization, orientation of the easy axis of magnetization, and the long-range magnetic order of the system in the function of the temperature. We distinguish magnetic components that emerge from the complex morpho-structural features of the undulating Fe or FeCo nanostructured films on trenched Mo templates: (i) assembly of magnetic nanowires and (ii) assembly of magnetic islands/clusters. Uniaxial anisotropy at room temperature was proven, characterized, and explained in the case of all systems. Our work contributes to the understanding of magnetic properties necessary for possible further applications of linear systems and undulated thin films.

A comparative study of morpho-structural, magnetic and magneto-transport properties of two Fe–Au granular films with different concentrations of Fe nanoclusters of almost similar size is reported. Different organizations of the Fe clusters, i.e. in lamellar-like or random-like configuration, were obtained by varying the amount of Fe in the Fe–Au films. The specific magnetic behaviour was investigated with respect to local structure and morpho-structural aspects by combining magneto-optic Kerr effect and superconducting quantum interference device magnetometry, ⁵⁷ Fe conversion electron Mössbauer spectroscopy and a wide range of electron microscopy techniques. A strong in-plane magnetic texture with uniaxial anisotropy was observed in the case of the lamellar-like organization of the clusters (specific to the Fe–Au film with higher Fe concentration) whereas a superparamagnetic behaviour was evidenced in the case of random distribution of the clusters (specific to the Fe–Au film with lower Fe concentration), despite the similar average size of the clusters in the two samples. Specific magnetoresistance effects were investigated with respect to both the involved magnetic configurations and magnetic interactions of the Fe clusters.

We report the facile and low-cost preparation as well as detailed characterization of dense arrays of passivated ferromagnetic nickel (Ni) nanotubes (NTs) vertically-supported onto solid Au-coated Si substrates. The proposed fabrication method relies on electrochemical synthesis within the nanopores of a supported anodic aluminum oxide (AAO) template and allows for fine tuning of the NTs ferromagnetic walls just by changing the cathodic reduction potential during the nanostructures’ electrochemical growth. Subsequently, the experimental platform allowed further passivation of the Ni NTs with the formation of ultra-thin antiferromagnetic layers of nickel oxide (NiO). Using adequately adapted magnetic measurements, we afterwards demonstrated that the thickness of the NT walls and of the thin antiferromagneticNiO layer, strongly influences the magnetic behavior of the dense array of exchange-coupled Ni/NiO NTs. The specific magnetic properties of these hybrid ferromagnetic/antiferromagnetic nanosystems were then correlated with the morpho-structural and geometrical parameters of the NTs, as well as ultimately strengthened by additionally-implemented micromagnetic simulations. The effect of the unidirectional anisotropy strongly amplified by the cylindrical geometry of the ferromagnetic/antiferromagnetic interfaces has been investigated with the magnetic field applied both parallel and perpendicular to the NTs axis.