A research study was conducted to establish the effect of the presence of sodium bis-2-ethyl-hexyl-sulfosuccinate (DOSS) surfactant on the size, shape, and magnetic properties of cobalt ferrite nanoparticles, and also on their ability to remove anionic dyes from synthetic aqueous solutions. The effect of the molar ratio cobalt ferrite to surfactant (1:0.1; 1:0.25 and 1:0.5) on the physicochemical properties of the prepared cobalt ferrite particles was evaluated using different characterization techniques, such as FT-IR spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N₂ adsorption-desorption analysis, and magnetic measurements. The results revealed that the surfactant has a significant impact on the textural and magnetic properties of CoFe₂O₄. The capacity of the synthesized CoFe₂O₄ samples to remove two anionic dyes, Congo Red (CR) and Methyl Orange (MO), by adsorption from aqueous solutions and the factors affecting the adsorption process, such as contact time, concentration of dyes in the initial solution, pH of the media, and the presence of a competing agent were investigated in batch experiments. Desorption experiments were performed to demonstrate the reusability of the adsorbents.

The use of bio-based reagents for silver nanoparticle (AgNP) production has gained much attention among researchers as it has paved the way for environmentally friendly approaches at low cost for synthesizing nanomaterials while maintaining their properties. In this study, Stellaria media aqueous extract was used for silver nanoparticle phyto-synthesis, and the resulting treatment was applied to textile fabrics to test its antimicrobial properties against bacteria and fungi strains. The chromatic effect was also established by determining the L*a*b* parameters. For optimizing the synthesis, different ratios of extract to silver precursor were tested using UV-Vis spectroscopy to observe the SPR-specific band. Moreover, the AgNP dispersions were tested for their antioxidant properties using chemiluminescence and TEAC methods, and the phenolic content was evaluated by the Folin-Ciocâlteu method. For the optimal ratio, values of average size, 50.11 ± 3.25 nm, zeta potential, −27.10 ± 2.16 mV, and polydispersity index, 0.209, were obtained via the DLS technique and zeta potential measurements. AgNPs were further characterized by EDX and XRD techniques to confirm their formation and by microscopic techniques to evaluate their morphology. TEM measurements revealed cvasi-spherical particles with sizes in the range of 10–30 nm, while SEM images confirmed their uniform distribution on the textile fiber surface.

This work is focused on a novel class of hybrid materials exhibiting enhanced optical properties and high surface areas that combine the morphology offered by the vinyl substituted silica host, and the excellent absorption and emission properties of 5,10,15,20-tetrakis(N-methyl-4-pyridyl)porphyrin-Zn(II) tetrachloride as a water soluble guest molecule. In order to optimize the synthesis procedure and the performance of the immobilized porphyrin, silica precursor mixtures of different compositions were used. To achieve the requirements regarding the hydrophobicity and the porous structure of the gels for the successful incorporation of porphyrin, the content of vinyltriacetoxysilane was systematically changed and thoroughly investigated. Substitution of the silica gels with organic groups is a viable way to provide new properties to the support. An exhaustive characterization of the synthesized silica samples was realised by complementary physicochemical methods, such as infrared spectroscopy (FT-IR), absorption spectroscopy (UV-Vis) and photoluminescence, nuclear magnetic resonance spectroscopy (29Si-MAS-NMR) transmission and scanning electron microscopy (TEM and SEM), nitrogen absorption (BET), contact angle (CA), small angle X ray and neutron scattering (SAXS and SANS). All hybrids showed an increase in emission intensity in the wide region from 575 to 725 nm (Q bands) in comparison with bare porphyrin. By simply tuning the vinyltriacetoxysilane content, the hydrophilic/hydrophobic profile of the hybrid materials was changed, while maintaining a high surface area. Good control of hydrophobicity is important to enhance properties such as dispersion, stability behaviour, and resistance to water, in order to achieve highly dispersible systems in water for biomedical applications.

Epitaxial La_0.7Sr_0.3MnO₃ films with different thicknesses (9–90 nm) were deposited on SrTiO₃ (0 0 1) substrates by pulsed laser deposition. The films have been investigated with respect to morpho-structural, magnetic, and magneto-transport properties, which have been proven to be thickness dependent. Magnetic contributions with different switching mechanisms were evidenced, depending on the perovskite film thickness. The Curie temperature increases with the film thickness. In addition, colossal magnetoresistance effects of up to 29% above room temperature were evidenced and discussed in respect to the magnetic behavior and film thickness.