Tannin foams are green lightweight materials that have attracted industrial interest for the manufacturing of sandwich panels for insulation purposes. However, the dimensions of the cells and the presence of sulfur in the formulation developed until now have discouraged their upscaling. In this work, we present the synthesis and the characterization of the more promising small cell and sulfur-free materials. It was observed that, with respect to standard ones, foams catalyzed with nitric acid present similar physical properties and more phenolic character, which favors the absorption of ionic pollutants. Conversely, the foams blown with aliphatic solvents and surfactants present smaller pores, and higher mechanical and insulating properties, without affecting the chemical properties or the heating value. The combined foam produced with nitric acid as a catalyst and petroleum ether as a blowing agent result in sulfur-free and small cell material with overall improved features. These foams have been produced at 30 × 30 × 3 cm³, with high homogeneity and, to date, they represent the most suitable formulation for industrial upscaling.

This study examined the potential of hydrolysable tannin in comparison to condensed tannins for the production of furanic foams. The results indicate that chestnut tannin presents lower reactivity and requires a stronger acid for the polymerization. Additionally, foamability and density were found to be dependent on both surfactant concentration and tannin type, allowing lower densities for mimosa tannin and lower thermal conductivities for chestnut-based foams. Mimosa tannin was found to have the highest compression strength, followed by quebracho and chestnut, promising thermal conductivity of around 50 mW/m·K for 300 kg/m³ foams, which suggests that chestnut foams have the potential to performing highly when the density is reduced. Chemical analysis revealed that the methylene moieties of the furanics are non-specific and produces new covalent bonds with nucleophilic substrates: -OH groups and free-positions in the flavonoids. Overall, this study opens new perspectives for the application of hydrolysable tannins in polymer and material science.

Tannin- and lignin-furanic foams are natural porous materials that have attracted high interest in the scientific and industrial communities for their high thermal and fire-resistant properties. However, no interesting solutions have been proposed for the management of their end-life as yet. In this study, the phenolic-furanic powders derived from the foams were analyzed for their capacity to remove different pollutants like neutral, cationic, and anionic organic molecules from wastewater. It was observed that the macromolecules produced from initially bigger fractions were more suitable to remove methylene blue and sodium dodecyl sulfate (SDS) while contained absorptions were observed for riboflavin. Acidified tannin powders were also prepared to understand the role of the flavonoid in the absorption mechanism. The latter showed outstanding absorption capacity against all of the tested pollutants, highlighting the key-role of the flavonoid fraction and suggesting the limited contribution of the furanic part. All adsorbents were investigated through FT-IR and solid state ¹³C-NMR. Finally, the powders were successfully regenerated by simple ethanol washing, showing almost complete absorption recovery.

Rising energy and raw material prices, dwindling resources, increased recycling, and the need for sustainable management have led to growth in the smart materials sector. In recent years, the importance and diversity of bio-based adhesives for industrial applications has grown steadily. This article focuses on the production and characterization of insulation panels consisting of peat moss and two bio-based adhesives. The panels were pressed with tannin and animal-based resins and compared to panels bonded with urea formaldehyde. The physical–mechanical properties, namely, thermal conductivity (TC), water vapor diffusion resistance, modulus of rupture (MOR), modulus of elasticity (MOE), internal bond (IB), compression resistance (CR), water absorption (WA) and thickness swelling (TS) were measured and analyzed. The results show that the insulation effectiveness and mechanical stability of moss panels bound with tannin and animal glue are comparable to standard adhesives used in the composite industry.

Tannins are well-known to protect plants from bacteria and fungi, but nothing is known about its effects on microorganisms once they are copolymerized. Therefore, a study was conducted to evaluate the effect of a tannin–furanic polymer in comparison with industrial mimosa tannin extract on the in vitro growth of two strains of bacteria, Bacillaceae and Pseudomanadaceae, and two white-rot fungi, Trametes versicolor and Agrocybe aegerita. Results have highlighted that the tannin polymer did not inhibit the growth of tested bacteria and even favored the growth of Bacillaceae without extra glucose. The growth of both fungi was enhanced by mimosa tannin and its polymer at low concentrations (<1%), while concentrations above 10% had a growth-inhibiting effect, which was slightly less strong for the polymer compared to the tannin against Trametes versicolor. These findings highlighted that tannin–furanic polymers can be tolerated by certain microorganisms at low concentration and that their inhibitory effect is similar or slightly lower than that of the pristine tannin extract.

Tannin-based foams have gained attention as a potential bio-based alternative to conventional synthetic foams. Traditionally, namely condensed tannins (CT) have been used, leaving the potential of hydrolysable tannins (HT) largely unexplored. This study compared the performance of chestnut (HT) and quebracho (CT) in tannin–protein-based foams at different tannin ratios. Using soy protein isolate (SPI) and hexamine under acidic conditions, a series of tannin foams were produced through a mechanical foaming method and analyzed for cell structure, compression strength, thermal conductivity, and chemical stability. Results show that chestnut tannin is viable in hexamine SPI formulations but is harder to process due to lower reactivity, further resulting in higher material densities compared to quebracho. Foams with higher quebracho content featured smaller, more interconnected cells, while increasing chestnut content led to larger, less interconnected cells. Compression strength decreased with higher chestnut content, while fire resistance and thermal conductivity were influenced by material density rather than tannin type. The ¹³C-NMR analysis revealed covalent bonding of hexamine with both tannins, but potential covalent bonds with SPI were undetectable. Overall, chestnut tannin can substitute quebracho tannin in hexamine-SPI foams, though with compromises in terms of specific material properties and processability.