In this study, composite anion exchange membranes (AEMs) were synthesized by cross-linking poly(phenylene oxide) (PPO) with cellulose functionalized by 1,4-diazabicyclo[2.2.2]-octane (DABCO) or di-guanidine (DG). The structural and morphological characteristics of the synthesized AEMs were characterized by FTIR, ¹H-NMR, SEM, TEM, and AFM, while their performance was evaluated in terms of ionic conductivity, water uptake, ion exchange capacity, and tensile strength with respect to the loading of the quaternized cellulose in the quaternized PPO (qPPO) matrix. The composite AEMs exhibited considerably enhanced mechanical and alkaline stability as well as good anion conductivity. The composite AEM with 7 wt% of cellulose functionalized with DG in the qPPO matrix (qPPO/DG-Cel7) exhibited a maximum hydroxide conductivity of 0.164 S cm⁻¹. Furthermore, a urea/O₂ fuel cell prepared using this composite membrane showed a maximum power density of 12.3 mW cm⁻². The results indicated that the cellulose-based composite membranes showed a satisfactory performance in alkaline fuel cell applications.

Anion-conducting membranes were obtained following the cross-linking of 1,4-diazoniabicycle[2.2.2]octane functionalized-polysulfone with N,N-dimethyl chitosan (DMC). The ionic conductivity of the composite membranes was controlled by the amount of DMC. The influence of the amount of DMC on water uptake, swelling ratio, and ionic conductivity of the obtained membrane was studied. The membrane with 2 wt% DMC exhibited an ionic conductivity of 54 mS/cm and 94 mS/cm at 25 °C and 70 °C, respectively. The membrane showed good dimensional stability under hydrated conditions. A urea/O₂ fuel cell, built using the composite membrane, exhibited a peak power density of 4.4 mW/cm² with a current density of 16.22 mA/cm² at 70 °C.

A nanofiber mat of styrene−co−vinylbenzyl chloride−co−acrylonitrile copolymer as an anion exchange membrane (AEM) was synthesized via the electrospinning of organic reaction mixtures. The synthesized membranes were characterized using FT-IR spectroscopy for structural analysis. The AEM demonstrated a high ionic conductivity mainly due to the phase segregation in the membrane structure, as analyzed by transmission electron microscopy (TEM). The membrane properties such as water uptake, swelling ratio, and ion exchange capacity, as well as ionic conductivity, varied with the chemical composition. With the molar ratio of styrene, vinylbenzyl chloride, and acrylonitrile at 3:5:2, the highest ionic conductivity of 0.214 S cm⁻¹ at 80 °C was observed. Additionally, the AEM retained 94% of original conductivity after 72 h of soaking in 1 M KOH solution.