Halloysite nanotube (HNT) additions to the thermoplastic polyurethane (TPU) system were thoroughly evaluated in this study. The resultant composites have been designed for future personalized intervertebral disc implant applications, which requires additional technology to obtain the appropriate geometry unique to each patient. These requirements can be fulfilled using 3D printing. In this work, a technology was developed to produce filaments for fused deposition modeling (FDM). Nanocomposites were prepared using variable HNT content (1, 2, and 3 wt.%). The nanostructure of the resultant composites was confirmed using scanning transmission electron microscopy (STEM). Mechanical tests were used to measure the tensile modulus, stress, and elongation the composites and TPU matrix. Nanocomposites with 2% HNT content were able to withstand 26% increased stress and 50% increased elongation compared to pure TPU before fracturing in addition to a 13% reduction in the friction coefficient. A MTT cytotoxicity assay confirmed the cytotoxicity of all tested materials against human epidermal keratinocyte cells (HaCaT).

Eco-friendly composites are proposed to substitute commonly available polymers. Currently, wood–plastic composites and natural fiber-reinforced composites are gaining growing recognition in the industry, being mostly on the thermoplastic matrix. However, little data are available about the possibility of producing biocomposites on a silicone matrix. This study focused on assessing selected organic fillers’ impact (ground coffee waste (GCW), walnut shell (WS), brewers’ spent grains (BSG), pistachio shell (PS), and chestnut (CH)) on the physicochemical and mechanical properties of silicone-based materials. Density, hardness, rebound resilience, and static tensile strength of the obtained composites were tested, as well as the effect of accelerated aging under artificial seawater conditions. The results revealed changes in the material’s properties (minimal density changes, hardness variation, overall decreasing resilience, and decreased tensile strength properties). The aging test revealed certain bioactivities of the obtained composites. The degree of material degradation was assessed on the basis of the strength characteristics and visual observation. The investigation carried out indicated the impact of the filler’s type, chemical composition, and grain size on the obtained materials’ properties and shed light on the possibility of acquiring ecological silicone-based materials.

This paper presents the results of research concerning multilayered epoxy composites reinforced with different materials. The strength of multilayered composites depends, to a large extent, on the reinforcing material. The authors decided to compare the low velocity impact response and perform tensile strength tests on several composites, to ascertain the mechanical properties of the prepared composites. Five different reinforcing materials were provided for the research (two fabrics made from aramid fibers, two fabrics made from carbon fibers and one fabric made from polyethylene fibers). The composites were manufactured by the vacuum supported hand laminating method. The low velocity impact response tests were conducted with the use of a pneumatic launcher. Three strikers with different geometry (conical striker, hemispherical striker and ogival striker) were used. A comparison of the resulting damage to the composites after the impact of the strikers was based on the images obtained using an optical microscope; tensile tests were also performed. The experimental investigation showed significant differences in the mechanical properties of the composites, depending on the applied reinforcing material. It was found that, as a result of the impacts, less damage occurred in the composites which were characterized by a lower Young’s modulus and a higher tensile strength.

The paper presents results obtained by experimental and numerical research focusing on the influence of the strikers’ geometry at the images of the destruction created in hybrid composite panels after applying impact load. In the research, the authors used four strikers with different geometry. The geometries were designed to keep the same weight for each of them. The composite panels used in the experiment were reinforced with aramid and carbon fabrics. An epoxy resin was used as a matrix. The experiments were carried with an impact kinetic energy of 23.5 J. The performed microscopy tests allowed for determination of destruction mechanisms of the panels depending on the geometry of the striker. The numerical calculations were performed using the finite element method. Each reinforcement layer of the composite was modeled as a different part. The bonded connection between the reinforcement layers was modeled using bilateral constraints. That approach enabled engineers to observe the delamination process during the impact. The results obtained from experimental and numerical investigations were compared. The authors present the impact of the striker geometry on damage formed in a composite panel. Formed damage was discussed. On the basis of the results from numerical research, energy absorption of the composite during impact depending on the striker geometry was discussed. It was noted that the size of the delamination area depends on the striker geometry. It was also noted that the diameter of the delamination area is related to the amount of damage in the reinforcing layers.

The impact of wood waste on the mechanical and biological properties of silicone-based composites was investigated using wood waste from oak, hornbeam, beech, and spruce trees. The density, abrasion resistance, resilience, hardness, and static tensile properties of the obtained WPC (wood–plastic composites) were tested. The results revealed slight changes in the density, increased abrasion resistance, decreased resilience, increased hardness, and decreased strain at break and stress at break compared with untreated silicone. The samples also showed no cytotoxicity to normal human dermal fibroblast, NHDF. The possibility of using prepared composites as materials to create structures on the seabed was also investigated by placing samples in a marine aquarium for one week and then observing sea algae growth.